Cathode slurry for secondary battery

ABSTRACT

A cathode slurry comprises a cathode active material, especially a nickel-containing cathode active material, a binder, a solvent and a base having a formula of R  1 R  2 R  3 N, with improved stability in water. Pre-treatment of nickel-containing cathode active materials may improve stability of the cathode by preventing undesirable decomposition of the material. In addition, battery cells comprising the cathode prepared by the cathode slurry exhibit impressive electrochemical performances.

FIELD OF THE INVENTION

The present invention relates to the field of batteries. In particular, this invention relates to cathode slurries for lithium-ion batteries.

BACKGROUND OF THE INVENTION

Over the past decades, lithium-ion batteries (LIBs) have become to be widely utilized in various applications, especially consumer electronics, because of their outstanding energy density, long cycle life and high discharging capability. Due to rapid market development of electric vehicles (EV) and grid energy storage, high-performance, low-cost LIBs are currently offering one of the most promising options for large-scale energy storage devices.

The use of multi-element lithium transition metal oxide such as lithium nickel manganese cobalt oxide (NMC) and lithium nickel cobalt aluminum oxide (NCA) has become popular due to their superior electrochemical properties over traditional cathode active material such as LiMnO₂, LiCoO₂, and LiNiO₂. Such superior electrochemical properties include a high energy density and superior capacity performance.

Currently, cathodes are often prepared by dispersing a cathode active material, binder material and conductive agent in an organic solvent such as N-methyl-2-pyrrolidone (NMP) to form a cathode slurry, then coating the cathode slurry onto a current collector and drying it.

The use of aqueous solutions instead of organic solvents is preferred for environmental reasons and easier handling and therefore water-based slurries have been considered. However, nickel-containing cathode active materials can react with water during electrode preparation, which causes metals in the cathode active material to leach out of the cathode active material and leads to performance degradation. Lithium dissolution at the surface of the cathode active material results in the formation of soluble bases. The high soluble base content raises the pH of the cathode slurry, which may affect dispersion homogeneity of the components (e.g., cathode active material) in the cathode slurry and binding strength of the binder material. It can also have negative effects on the metallic components of the electrode (e.g., the current collector) and adversely affects the performance of the cathode active material. For example, the cathode active material will react with aluminum foil current collectors to produce Al(OH)₃ precipitate, which will hinder the transfer of lithium ions, thereby reducing the battery capacity retention rate. These factors all contribute to poor electrochemical performance. Conventionally, a pH modifier is used to adjust the pH of the cathode slurry. However, such additives may also have a deleterious effect on the electrochemical processes that take place at the cathode, especially at higher voltages and temperatures, which in turn diminishes battery performance. Accordingly, it is desirable to prevent lithium dissolution from the surface of the cathode active material in the process of the cathode slurry preparation.

EP Patent Application Publication No. 3044822 A discloses a water-based lithium transition metal oxide cathode slurry. The slurry comprises a lithium transition metal oxide powder, which consists of primary particles comprising a polymer-containing coating layer. The coating layer is composed of two layers. The outer layer contains a fluorine-containing polymer that prevents the pH-raising ion exchange reaction with water by reducing surface coverage of water. The inner layer contains a product, such as LiF, of the reaction between the polymer of the outer layer and the lithium transition metal oxide, where the reaction decomposes the surface base and reduces the base potential of the oxide. However, the fluorine-containing polymers increase electrical resistance, which leads to reduced battery performance, as well as pose risks to the health of people and the environment.

In view of the above, there is always a need to develop a method for preparing cathode slurries having a nickel-containing cathode active material for lithium-ion batteries with good electrochemical performance using a simple, fast and environmentally-friendly method.

SUMMARY OF THE INVENTION

The aforementioned needs are met by various aspects and embodiments disclosed herein. Provided herein is a cathode slurry for a secondary battery, comprising a cathode active material, a binder, a solvent and a base having a formula of R¹R²R³N, wherein each of R¹, R² and R³ is independently H, C₁₋₆ alkyl, C₃₋₆ cycloalkyl, C₁₋₆ heteroalkyl, C₄₋₆ cycloalkylalkyl, C₂₋₆ alkoxyalkyl, or C₃₋₆ alkoxyalkoxyalkyl, where the C₁₋₆ alkyl, C₃₋₆ cycloalkyl, C₁₋₆ heteroalkyl, C₄₋₆ cycloalkylalkyl, C₂₋₆ alkoxyalkyl, or C₃₋₆ alkoxyalkoxyalkyl is optionally substituted with one or more substituents, where each of the substituents is independently alkyl or cycloalkyl.

In some embodiments, each of R¹, R² and R³ is independently C₁₋₄ alkyl, C₃₋₅ cycloalkyl, C₁₋₄ heteroalkyl, C₂₋₄ alkoxyalkyl, or C₃₋₅ alkoxyalkoxyalkyl. In other embodiments, each of R¹, R² and R³ is independently H, methyl, ethyl, propyl, isopropyl, cyclopropyl, n-butyl, tert-butyl, isobutyl, sec-butyl, cyclobutyl, pentyl, methoxymethyl, ethoxymethyl, or methoxyethoxymethyl. In certain embodiments, the base is selected from the group consisting of ammonia, methylamine, ethylamine, propylamine, isopropylamine, cyclopropylamine, butylamine, N-butylamine, tert-butylamine, isobutylamine, sec-butylamine, cyclobutylamine, dimethylamine, N-ethylmethylamine, diethylamine, N-methylpropylamine, N-methylcyclopropanamine, N-ethyl-N-propylamine, N,2-dimethyl-1-propanamine, N-tert-butylmethylamine, diisopropylamine, N-methyl-tert-butylamine, trimethylamine, N,N-dimethylethylamine, N,N-diethylmethylamine, N,N-dimethylisopropylamine, triethylamine and combinations thereof.

In certain embodiments, the cathode active material is selected from the group consisting of Li_(1+x)Ni_(a)Mn_(b)Co_(c)Al_((1−a−b−c))O₂, LiNi_(0.33)Mn_(0.33)Co_(0.33)O₂, LiNi_(0.4)Mn_(0.4)Co_(0.2)O₂, LiNi_(0.5)Mn_(0.3)Co_(0.2)O₂, LiNi_(0.6)Mn_(0.2)Co_(0.2)O₂, LiNi_(0.7)Mn_(0.15)Co_(0.15)O₂, LiNi_(0.8)Mn_(0.1)Co_(0.1)O₂, LiNi_(0.92)Mn_(0.04)Co_(0.04)O₂, LiNi_(0.8)Co_(0.15)Al_(0.05)O₂, LiCoO₂, LiNiO₂, LiMnO₂, LiMn₂O₄, Li₂MnO₃, and combinations thereof, wherein −0.2≤x≤0.2, 0≤a<1, 0≤b<1, 0≤c<1, and a+b+c≤1.

In some embodiments, the cathode active material comprises or is a core-shell composite having a core and shell structure, wherein the core and the shell each independently comprise a lithium transition metal oxide selected from the group consisting of Li_(1+x)Ni_(a)Mn_(b)Co_(c)Al_((1−a−b−c))O₂, LiCoO₂, LiNiO₂, LiMnO₂, LiMn₂O₄, Li₂MnO₃, LiCrO₂, Li₄Ti₅O₁₂, LiV₂O₅, LiTiS₂, LiMoS₂, and combinations thereof, wherein −0.2≤x≤0.2, 0≤a<1, 0≤b<1, 0≤c<1, and a+b+c≤1.

In certain embodiments, lithium loss of the cathode active material is inhibited by a percentage from about 1 percent to about 50 percent.

In some embodiments, the solvent is water or a mixture of water and an alcohol. In certain embodiments, the alcohol is selected from the group consisting of ethanol, isopropanol, n-propanol, tert-butanol, n-butanol, and combinations thereof. In some embodiments, the alcohol comprises from about 1% to about 30% of the total weight of the cathode slurry.

In certain embodiments, the cathode slurry further comprises a conductive agent that is selected from the group consisting of carbon, carbon black, graphite, expanded graphite, graphene, graphene nanoplatelets, carbon fibers, carbon nano-fibers, graphitized carbon flake, carbon tubes, carbon nanotubes, activated carbon, mesoporous carbon and combinations thereof.

In some embodiments, the binder material is selected from the group consisting of styrene-butadiene rubber, carboxymethyl cellulose, polyvinylidene fluoride, acrylonitrile copolymer, polyacrylic acid, polyacrylonitrile, poly(vinylidene fluoride)-hexafluoropropene, LA132, LA133, LA138, latex, a salt of alginic acid, and combinations thereof. In further embodiments, the salt of alginic acid comprises a cation selected from the group consisting of Na, Li, K, Ca, NH₄, Mg, Al, and combinations thereof.

In certain embodiments, the boiling point of the base is lower than 100° C. at a pressure of 1 atm. In certain embodiments, the concentration of the base in the cathode slurry is from about 0.5% to about 3.5% by weight, based on the total weight of the cathode slurry.

In some embodiments, the pH of the cathode slurry is from about 8 to about 14. In some embodiments, the solid content of the cathode slurry is from about 45% to about 75% by weight, based on the total weight of the cathode slurry.

In certain embodiments, the cathode slurry is free of a dispersing agent selected from the group consisting of a cationic surfactant, an anionic surfactant, a nonionic surfactant, an amphoteric surfactant, and a polymeric acid.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a flow chart of an embodiment illustrating the steps for preparing a cathode.

FIG. 2 depicts the D50 particle size distribution of the organic and base-treated slurries respectively.

FIG. 3 is a graph showing the relationship between the concentration of lithium ions in the cathode slurry and time.

FIGS. 4 a and 4 b depict the appearance of the surface of cathode electrode layers after coating with the untreated and base-treated slurries respectively.

FIG. 5 is a bar graph showing the peeling strengths of electrodes prepared by different methods.

FIG. 6 shows three specific capacity-voltage curves of the first discharge cycle of NMC811.

DETAILED DESCRIPTION OF THE INVENTION

Provided herein is a method of preparing a cathode slurry for a secondary battery, comprising a cathode active material, a binder, a solvent and a base having a formula of R¹R²R³N, wherein each of R¹, R² and R³ is independently H, C₁₋₆ alkyl, C₃₋₆ cycloalkyl, C₁₋₆ heteroalkyl, C₄₋₆ cycloalkylalkyl, C₂₋₆ alkoxyalkyl, or C₃₋₆ alkoxyalkoxyalkyl, where the C₁₋₆ alkyl, C₃₋₆ cycloalkyl, C₁₋₆ heteroalkyl, C₄₋₆ cycloalkylalkyl, C₂₋₆ alkoxyalkyl, or C₃₋₆ alkoxyalkoxyalkyl is optionally substituted with one or more substituents, where each of the substituents is independently alkyl or cycloalkyl.

The term “electrode” refers to a “cathode” or an “anode.”

The term “positive electrode” is used interchangeably with cathode. Likewise, the term “negative electrode” is used interchangeably with anode.

The term “binder material” refers to a chemical or a substance used to hold an electrode material and/or a conductive agent in place and adhere them onto a conductive metal part to form an electrode. In some embodiments, the electrode does not comprise any conductive agent.

The term “conductive agent” refers to a material which is chemically inactive and has good electrical conductivity. Therefore, the conductive agent is often mixed with an electrode active material at the time of forming an electrode to improve electrical conductivity of the electrode.

The term “homogenizer” refers to an equipment that can be used for homogenization of materials. The term “homogenization” refers to a process of distributing the materials uniformly throughout a fluid. Any conventional homogenizers can be used for the method disclosed herein. Some non-limiting examples of the homogenizer include stirring mixers, planetary stirring mixers, blenders and ultrasonicators.

The term “planetary mixer” refers to an equipment that can be used to mix or stir different materials for producing a homogeneous mixture, which consists of blades conducting a planetary motion within a vessel. In some embodiments, the planetary mixer comprises at least one planetary blade and at least one high-speed dispersion blade. The planetary and the high-speed dispersion blades rotate on their own axes and also rotate continuously around the vessel. The rotation speed can be expressed in unit of rotations per minute (rpm) which refers to the number of rotations that a rotating body completes in one minute.

The term “applying” refers to an act of laying or spreading a substance on a surface.

The term “current collector” refers to any conductive substrate, which is in contact with an electrode layer and is capable of conducting an electrical current flowing to electrodes during discharging or charging a secondary battery. Some non-limiting examples of the current collector include a single conductive metal layer or substrate and a single conductive metal layer or substrate with an overlying conductive coating layer, such as a carbon black-based coating layer. The conductive metal layer or substrate may be in the form of a foil or a porous body having a three-dimensional network structure, and may be a polymeric or metallic material or a metalized polymer. In some embodiments, the three-dimensional porous current collector is covered with a conformal carbon layer.

The term “electrode layer” refers to a layer, which is in contact with a current collector, that comprises an electrochemically active material. In some embodiments, the electrode layer is made by applying a coating on to the current collector. In some embodiments, the electrode layer is located on the surface of the current collector. In other embodiments, the three-dimensional porous current collector is coated conformally with an electrode layer.

The term “doctor blading” refers to a process for fabrication of large area films on rigid or flexible substrates. A coating thickness can be controlled by an adjustable gap width between a coating blade and a coating surface, which allows the deposition of variable wet layer thicknesses.

The term “slot-die coating” refers to a process for fabrication of large area films on rigid or flexible substrates. A slurry is applied to the substrate by continuously pumping slurry through a nozzle onto the substrate, which is mounted on a roller and constantly fed toward the nozzle. The thickness of the coating is controlled by various methods, such as altering the slurry flow rate or the speed of the roller.

The term “room temperature” refers to indoor temperatures from about 18° C. to about 30° C., e.g., 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, or 30° C. In some embodiments, room temperature refers to a temperature of about 20° C.+/−1° C. or +/−2° C. or +/−3° C. In other embodiments, room temperature refers to a temperature of about 22° C. or about 25° C.

The term “particle size D50” refers to a volume-based accumulative 50% size (D50), which is a particle size at a point of 50% on an accumulative curve (i.e., a diameter of a particle in the 50th percentile (median) of the volumes of particles) when the accumulative curve is drawn so that a particle size distribution is obtained on the volume basis and the whole volume is 100%. Further, with respect to the cathode active material of the present invention, the particle size D50 means a volume-averaged particle size of secondary particles which can be formed by mutual agglomeration of primary particles, and in a case where the particles are composed of the primary particles only, it means a volume-averaged particle size of the primary particles.

The term “solid content” refers to the amount of non-volatile material remaining after evaporation.

The term “peeling strength” refers to the amount of force required to separate two materials that are bonded to each other, such as a current collector and an electrode active material coating. It is a measure of the adhesion strength between such two materials and is usually expressed in N/cm.

The term “C rate” refers to the charging or discharging rate of a cell or battery, expressed in terms of its total storage capacity in Ah or mAh. For example, a rate of 1 C means utilization of all of the stored energy in one hour; a 0.1 C means utilization of 10% of the energy in one hour or full energy in 10 hours; and a 5 C means utilization of full energy in 12 minutes.

The term “ampere-hour (Ah)” refers to a unit used in specifying the storage capacity of a battery. For example, a battery with 1 Ah capacity can supply a current of one ampere for one hour or 0.5 A for two hours, etc. Therefore, 1 Ampere-hour (Ah) is the equivalent of 3,600 coulombs of electrical charge. Similarly, the term “miniampere-hour (mAh)” also refers to a unit of the storage capacity of a battery and is 1/1,000 of an ampere-hour.

The term “battery cycle life” refers to the number of complete charge/discharge cycles a battery can perform before its nominal capacity falls below 80% of its initial rated capacity.

The term “capacity” is a characteristic of an electrochemical cell that refers to the total amount of electrical charge an electrochemical cell, such as a battery, is able to hold. Capacity is typically expressed in units of ampere-hours. The term “specific capacity” refers to the capacity output of an electrochemical cell, such as a battery, per unit weight, usually expressed in Ah/kg or mAh/g.

In the following description, all numbers disclosed herein are approximate values, regardless whether the word “about” or “approximate” is used in connection therewith. They may vary by 1 percent, 2 percent, 5 percent, or, sometimes, 10 to 20 percent. Whenever a numerical range with a lower limit, R^(L), and an upper limit, R^(U), is disclosed, any number falling within the range is specifically disclosed. In particular, the following numbers within the range are specifically disclosed: R=R^(L)+k*(R^(U)−R^(L)), wherein k is a variable ranging from 0 percent to 100 percent. Moreover, any numerical range defined by two R numbers as defined in the above is also specifically disclosed.

Generally, lithium-ion battery electrodes are manufactured by casting an organic-based slurry onto a metallic current collector. The slurry contains electrode active material, conductive carbon, and binder in an organic solvent, most commonly N-methyl-2-pyrrolidone (NMP). The binder, most commonly polyvinylidene fluoride (PVDF), is dissolved in the solvent, and conductive additives as well as the electrode active material are suspended in the slurry. PVDF provides a good electrochemical stability and high adhesion to the electrode materials and current collectors. However, PVDF can only dissolve in some specific organic solvents such as N-methyl-2-pyrrolidone (NMP) which is flammable and toxic and hence requires specific handling.

An NMP recovery system must be in place during the drying process to recover NMP vapors. This will generate significant costs in the manufacturing process since it requires a large capital investment. The use of less expensive and more environmentally-friendly solvents, such as aqueous solvents, is preferred since it can reduce the large capital cost of the recovery system. The attempts to replace the organic NMP-based coating process with a water-based coating process have been successful for the negative electrode. A typical water-based slurry for anode coating comprises carboxymethyl cellulose (CMC) and styrene-butadiene rubber (SBR). Within the battery, cathodes are at high voltage. Most rubbers including SBR are only stable at the low voltage of the anode and will decompose at high voltage. Therefore, contrary to anodes, water-based coating for cathodes is much more difficult.

Another concern of water-based processing is the fact that many cathode active materials are not inert in water, which causes problems and complicates the implementation of water-based coating process for cathodes. The lithium in cathode active materials may react with H₂O to generate LiOH, resulting in a degraded electrochemical performance. In general, the surface of the cathode active material is coated with an ion-conductive solid compound in order to enhance its stability toward and compatibility with water-based processing. Acid may also be added to the solution to adjust the slurry pH by neutralizing the base on the surface of the cathode active material. However, upon exposure to water, a significant amount of soluble base LiOH will continuously form, damaging the cathode active material at a significant rate.

Accordingly, the present invention provides a method of preparing a cathode via the use of a water-based slurry. FIG. 1 is a flow chart of an embodiment illustrating the steps of method 100 for preparing a cathode. The slurry prepared by the method disclosed herein shows improved stability by minimizing the reactivity of the cathode active material with water, thereby enhancing battery performance.

In some embodiments, the first suspension is formed by dispersing a cathode active material with an aqueous solution at step 101. In some embodiments, a cathode active material is dispersed in an aqueous solution to form a first suspension.

Conventional prior art processes for making cathode slurries may require a step to thoroughly dry the cathode active material or remove the chemical after pre-treatment. One advantage of this invention is that the cathode active material is combined with the base and other components such as binders to form a slurry as is, without drying or removing the base. This leads to faster, more efficient production.

Surprisingly, not all types of basic treatment before forming the cathode active material achieve the same desired effect of the present invention. The base should be added after completion of the formation of the cathode active material. In some embodiments, the base has a formula R¹R²R³N, wherein each of R¹, R² and R³ is independently H, C₁₋₆ alkyl, C₃₋₆ cycloalkyl, C₁₋₆ heteroalkyl, C₄₋₆ cycloalkylalkyl, C₂₋₆ alkoxyalkyl, or C₃₋₆ alkoxyalkoxyalkyl where the C₁₋₆ alkyl, C₃₋₆ cycloalkyl, C₁₋₆ heteroalkyl, C₄₋₆ cycloalkylalkyl, C₂₋₆ alkoxyalkyl, or C₃₋₆ alkoxyalkoxyalkyl is optionally substituted with one or more substituents, where each of the substituents is independently alkyl or cycloalkyl.

In some embodiments, the base has a formula R¹R²R³N, wherein each of R¹, R² and R³ is independently C₁₋₄ alkyl, C₃₋₅ cycloalkyl, C₁₋₄ heteroalkyl, C₂₋₄ alkoxyalkyl, or C₃₋₅ alkoxyalkoxyalkyl. In certain embodiments, the base is selected from a compound having formula R¹R²R³N, wherein each of R¹, R² and R³ is independently H, methyl, ethyl, propyl, isopropyl, cyclopropyl, n-butyl, tert-butyl, isobutyl, sec-butyl, cyclobutyl, pentyl, methoxymethyl, ethoxymethyl, or methoxyethoxymethyl.

In some embodiments, the base is ammonia, a primary amine, secondary amine, tertiary amine or a combination thereof. In some embodiments, the base is a primary amine selected from the group consisting of methylamine, ethylamine, propylamine, isopropylamine, cyclopropylamine, butylamine, N-butylamine, tert-butylamine, isobutylamine, sec-butylamine, cyclobutylamine and combinations thereof. In certain embodiments, the base is a secondary amine selected from the group consisting of dimethylamine, N-ethylmethylamine, diethylamine, N-methylpropylamine, N-methylcyclopropanamine, N-ethyl-N-propylamine, N,2-dimethyl-1-propanamine, N-tert-butylmethylamine, diisopropylamine and combinations thereof. In some embodiments, the base is a tertiary amine selected from the group consisting of trimethylamine, N,N-dimethylethylamine, N,N-diethylmethylamine, N,N-dimethylisopropylamine, triethylamine and combinations thereof.

In some embodiments, the pH of the first suspension is from about 8 to about 14, from about 8 to about 13.5, from about 8 to about 13, from about 8 to about 12.5, from about 8 to about 12, from about 8 to about 11.5, from about 8 to about 11, from about 8 to about 10.5, from about 8 to about 10, from about 8 to about 9, from about 8.5 to about 14, from about 8.5 to about 13, from about 8.5 to about 12, from about 8.5 to about 11, from about 8.5 to about 10.5, from about 9 to about 14, from about 9 to about 13, from about 9 to about 12, from about 9 to about 11, from about 9 to about 10, from about 10 to about 14, from about 10 to about 13, from about 10 to about 12, from about 10 to about 11, from about 11 to about 14, from about 11 to about 13, from about 11 to about 12, from about 12 to about 14, or from about 12 to about 13. In certain embodiments, the pH of the first suspension is less than 14, less than 13.5, less than 13, less than 12.5, less than 12, less than 11.5, less than 11, less than 10.5, less than 10, less than 9.5, less than 9, or less than 8.5. In some embodiments, the pH of the first suspension is greater than 8, greater than 8.5, greater than 9, greater than 9.5, greater than 10, greater than 10.5, greater than 11, greater than 11.5, greater than 12, greater than 12.5, greater than 13, or greater than 13.5.

The cathode active material is dispersed in the aqueous solution to form a first suspension, so that the cathode active material is treated with the base in the aqueous solution. When exposed to the base, the stability of the cathode active material in water is enhanced. It is desired and necessary to allow the cathode active material to be treated in the first suspension for some time before the addition of other electrode components such as binders and conductive agents. The cathode active material should be treated in the aqueous solution for less than about 1 hour. If the treating time is shorter than 1 minute, the cathode active material does not receive sufficient treatment, while treating times above 60 minutes may result in degradation of the cathode active material. In some embodiments, the cathode active material is treated with the aqueous solution for a time period from about 1 minute to about 60 minutes, from about 1 minute to about 50 minutes, from about 1 minute to about 40 minutes, from about 1 minute to about 30 minutes, from about 1 minute to about 20 minutes, from about 1 minute to about 10 minutes, from about 5 minutes to about 60 minutes, from about 5 minutes to about 50 minutes, from about 5 minutes to about 40 minutes, from about 5 minutes to about 30 minutes, from about 5 minutes to about 20 minutes, from about 5 minutes to about 10 minutes, from about 10 minutes to about 60 minutes, from about 10 minutes to about 50 minutes, from about 10 minutes to about 40 minutes, from about 10 minutes to about 30 minutes, from about 10 minutes to about 20 minutes, from about 15 minutes to about 60 minutes, from about 15 minutes to about 50 minutes, from about 15 minutes to about 40 minutes, from about 15 minutes to about 30 minutes, from about 15 minutes to about 20 minutes, from about 20 minutes to about 50 minutes, from about 20 minutes to about 40 minutes, or from about 20 minutes to about 30 minutes.

In certain embodiments, the cathode active material is treated with the aqueous solution for a time period less than 60 minutes, less than 55 minutes, less than 50 minutes, less than 45 minutes, less than 40 minutes, less than 35 minutes, less than 30 minutes, less than 25 minutes, less than 20 minutes, less than 15 minutes, less than 10 minutes, or less than 5 minutes. In some embodiments, the cathode active material is treated with the aqueous solution for a time period of more than about 55 minutes, more than about 50 minutes, more than about 45 minutes, more than about 40 minutes, more than about 35 minutes, more than about 30 minutes, more than about 25 minutes, more than about 20 minutes, more than about 15 minutes, more than about 10 minutes, or more than about 5 minutes.

After dispersing the cathode active material in the aqueous solution, the mixture may be stirred or left to rest to form the first suspension. In some embodiments, the mixture may be stirred or left to rest for a time period from about 10 minutes to 60 minutes, from about 15 minutes to about 60 minutes, from about 20 minutes to about 60 minutes, from about 30 minutes to about 60 minutes, from about 10 minutes to about 45 minutes, from about 10 minutes to about 30 minutes, or from about 20 minutes to about 45 minutes.

It is found that the treatment of the cathode active material with the aqueous solution should be performed at a temperature range from about 5° C. to about 35° C. in order to avoid undesired effects on battery performance, such as reduced capacity and cyclability performance. In some embodiments, the cathode active material is treated with the aqueous solution at a temperature range from about 5° C. to about 30° C., from about 5° C. to about 25° C., from about 5° C. to about 20° C., from about 5° C. to about 15° C., or from about 5° C. to about 10° C. In certain embodiments, the cathode active material is treated with the aqueous solution at a temperature of less than 30° C., less than 25° C., less than 20° C., less than 15° C., or less than 10° C. In some embodiments, the cathode active material is treated with the aqueous solution at a temperature of higher than about 25° C., higher than about 20° C., higher than about 15° C., higher than about 10° C., or higher than about 5° C.

The concentration of the base in the first suspension critically impacts the battery performance. In some embodiments, the concentration of the base in the aqueous solution is from about 1% to about 30% by weight, based on the total weight of the aqueous solution. In certain embodiments, the concentration of the base in the aqueous solution is from about 1% to about 25%, from about 1% to about 20%, from about 1% to about 15%, from about 1% to about 10%, from about 1% to about 5%, from about 4% to about 10%, from about 4% to about 8%, from about 5% to about 25%, from about 5% to about 20%, from about 5% to about 15%, from about 7% to about 15%, from about 7% to about 13%, from about 10% to about 25%, from about 10% to about 20%, from about 10% to about 15%, from about 15% to about 25%, or from about 15% to about 20% by weight, based on the total weight of the aqueous solution. In some embodiments, the amount of base in the aqueous solution is less than 30%, less than 25%, less than 20%, less than 15%, less than 10%, less than 5%, or less than 1% by weight, based on the total weight of the aqueous solution. In some embodiments, a low concentration of the base in the first suspension is insufficient to cause any noticeable changes in the battery performance. The concentration of the base in the aqueous solution should be higher than about 5%, about 6%, about 7%, about 8%, about 9%, about 10%, about 13%, about 15% or about 20% by weight, based on the total weight of the aqueous solution.

In some embodiments, the boiling point of the base is lower than or equal to the boiling point of water. When the coated film is oven dried, the base is often removed before the slurry solvent is substantially removed. In some embodiments, the boiling point of the base is lower than 100° C., lower than 90° C., lower than 80° C., lower than 70° C., lower than 60° C., lower than 50° C., lower than 40° C., lower than 30° C., lower than 20° C., lower than 10° C., or lower than 0° C., at a pressure of 1 atmosphere (atm). In certain embodiments, the boiling point of the base is higher than −40° C., higher than −30° C., higher than −20° C., higher than −10° C., higher than 10° C., higher than 20° C., higher than 30° C., higher than 40° C., higher than 50° C., higher than 60° C., higher than 70° C., higher than 80° C., or higher than 90° C., at a pressure of 1 atm. In some embodiments, the base has a boiling point between −40° C. and 100° C., between −40° C. and 80° C., between −40° C. and 60° C., between −40° C. and 50° C., between −40° C. and 40° C., between 10° C. and 90° C., between 10° C. and 80° C., between 20° C. and 80° C., between 20° C. and 50° C., or between −40° C. and 30° C., at a pressure of 1 atm.

In some embodiments, the active battery electrode material is a cathode active material, wherein the cathode active material is selected from the group consisting of LiCoO₂, LiNiO₂, LiNi_(x)Mn_(y)O₂, Li_(1+z)Ni_(x)Mn_(y)Co_(1−x−y)O₂, LiNi_(x)Co_(y)Al_(z)O₂, LiV₂O₅, LiTiS₂, LiMoS₂, LiMnO₂, LiCrO₂, LiMn₂O₄, LiFeO₂, LiFePO₄, and combinations thereof, wherein each x is independently from 0.3 to 0.8; each y is independently from 0.1 to 0.45; and each z is independently from 0 to 0.2. In certain embodiments, the cathode active material is selected from the group consisting of LiCoO₂, LiNiO₂, LiNi_(x)Mn_(y)O₂, Li_(1+z)Ni_(x)Mn_(y)Co_(1−x−y)O₂ (NMC), LiNi_(x)Co_(y)Al_(z)O₂, LiV₂O₅, LiTiS₂, LiMoS₂, LiMnO₂, LiCrO₂, LiMn₂O₄, LiFeO₂, LiFePO₄, and combinations thereof, wherein each x is independently from 0.4 to 0.6; each y is independently from 0.2 to 0.4; and each z is independently from 0 to 0.1. In other embodiments, the cathode active material is not LiCoO₂, LiNiO₂, LiV₂O₅, LiTiS₂, LiMoS₂, LiMnO₂, LiCrO₂, LiMn₂O₄, LiFeO₂, or LiFePO₄. In further embodiments, the cathode active material is not LiNi_(x)Mn_(y)O₂, Li_(1+z)Ni_(x)Mn_(y)Co_(1−x−y)O₂, or LiNi_(x)Co_(y)Al_(z)O₂, wherein each x is independently from 0.3 to 0.8; each y is independently from 0.1 to 0.45; and each z is independently from 0 to 0.2.

In certain embodiments, the cathode active material is doped with a dopant selected from the group consisting of Fe, Ni, Mn, Al, Mg, Zn, Ti, La, Ce, Sn, Zr, Ru, Si, Ge, and combinations thereof. In some embodiments, the dopant is not Fe, Ni, Mn, Mg, Zn, Ti, La, Ce, Ru, Si, or Ge. In certain embodiments, the dopant is not Al, Sn, or Zr.

The method disclosed herein is particularly suitable for preparing a cathode using a nickel-containing cathode active material. Nickel-containing cathodes prepared by the method disclosed herein have improved electrochemical performance and long-term stability.

In some embodiments, the cathode active material is Li_(1+x)Ni_(a)Mn_(b)Co_(c)Al_((1−a−b−c))O₂, LiNi_(0.33)Mn_(0.33)Co_(0.33)O₂(NMC333), LiNiO₄MnO₄Co_(0.2)O₂, LiNi_(0.5)Mn_(0.3)Co_(0.2)O₂ (NMC532), LiNi_(0.6)Mn_(0.2)Co_(0.2)O₂ (NMC622), LiNi_(0.7)Mn_(0.15)Co_(0.15)O₂, LiNi_(0.8)Mn_(0.1)Co_(0.1)O₂ (NMC811), LiNi_(0.92)Mn_(0.04)Co_(0.04)O₂, LiNi_(0.8)Co_(0.15)Al_(0.005)O₂ (NCA), LiCoO₂ (LCO), LiNiO₂ (LNO), LiMnO₂, LiMn₂O₄(LMO), Li₂MnO₃, and combinations thereof, wherein −0.2≤x≤0.2, 0≤a<1, 0≤b<1, 0≤c<1, and a+b+c≤1. In certain embodiments, the cathode active material is Li_(1+x)Ni_(a)Mn_(b)Co_(c)Al_((1−a−b−c))O₂; wherein −0.2≤x≤0.2, 0≤a<1, 0≤b<1, 0≤c<1, and a+b+c<1. In some embodiments, the cathode active material has the general formula Li_(1+x)Ni_(a)Mn_(b)Co_(c)Al_((1−a−b−c))O₂, with 0.33≤a≤0.92, 0.33≤a≤0.9, 0.33≤a≤0.8, 0.5≤a≤0.92, 0.5≤a≤0.9, 0.5≤a≤0.8, 0.6≤a≤0.92, or 0.6≤a≤0.9; 0≤b≤0.5, 0≤b≤0.3, 0.1≤b≤0.5, 0.1≤b≤0.4, 0.1≤b≤0.3, 0.1≤b≤0.2, or 0.2≤b≤0.5; 0≤c≤0.5, 0≤c≤0.3, 0.1≤c≤0.5, 0.1≤c≤0.4, 0.1≤c≤0.3, 0.1≤c≤0.2, or 0.2≤c≤0.5.

In other embodiments, the cathode active material is not LiCoO₂, LiNiO₂, LiMnO₂, LiMn₂O₄, or Li₂MnO₃. In further embodiments, the cathode active material is not LiNi_(0.33)Mn_(0.33)Co_(0.33)O₂, LiNi_(0.4)Mn_(0.4)Co_(0.2)O₂, LiNi_(0.5)Mn_(0.3)Co_(0.2)O₂, LiNi_(0.6)Mn_(0.2)Co_(0.2)O₂, LiNi_(0.7)Mn_(0.15)Co_(0.15)O₂, LiNi_(0.8)Mn_(0.1)Co_(0.1)O₂, LiNi_(0.92)Mn_(0.04)Co_(0.04)O₂, or LiNi_(0.8)Co_(0.15)Al_(0.05)O₂.

In certain embodiments, the cathode active material comprises or is a core-shell composite having a core and shell structure, wherein the core and the shell each independently comprise a lithium transition metal oxide selected from the group consisting of Li_(1+x)Ni_(a)Mn_(b)Co_(c)Al_((1−a−b−c))O₂, LiCoO₂, LiNiO₂, LiMnO₂, LiMn₂O₄, Li₂MnO₃, LiCrO₂, Li₄Ti₅O₁₂, LiV₂O₅, LiTiS₂, LiMoS₂, and combinations thereof, wherein −0.2≤x≤0.2, 0≤a<1, 0≤b<1, 0≤c<1, and a+b+c<1. In other embodiments, the core and the shell each independently comprise two or more lithium transition metal oxides. In some embodiments, one of the core or shell comprises only one lithium transition metal oxide, while the other comprises two or more lithium transition metal oxides. The lithium transition metal oxide or oxides in the core and the shell may be the same, or they may be different or partially different. In some embodiments, the two or more lithium transition metal oxides are uniformly distributed over the core. In certain embodiments, the two or more lithium transition metal oxides are not uniformly distributed over the core. In some embodiments, the cathode active material is not a core-shell composite.

In some embodiments, each of the lithium transition metal oxides in the core and the shell is independently doped with a dopant selected from the group consisting of Fe, Ni, Mn, Al, Mg, Zn, Ti, La, Ce, Sn, Zr, Ru, Si, Ge, and combinations thereof. In certain embodiments, the core and the shell each independently comprise two or more doped lithium transition metal oxides. In some embodiments, the two or more doped lithium transition metal oxides are uniformly distributed over the core. In certain embodiments, the two or more doped lithium transition metal oxides are not uniformly distributed over the core.

In some embodiments, the diameter of the core is from about 5 μm to about 45 μm, from about 5 μm to about 35 μm, from about 5 μm to about 25 μm, from about 10 μm to about 40 μm, or from about 10 μm to about 35 μm. In certain embodiments, the thickness of the shell is from about 1 μm to about 45 μm, from about 1 μm to about 35 μm, from about 1 μm to about 25 μm, from about 1 μm to about 15 μm, from about 1 μm to about 10 μm, from about 1 μm to about 5 μm, from about 3 μm to about 15 μm, from about 3 μm to about 10 μm, from about 5 μm to about 10 μm, from about 10 μm to about 45 μm, from about 10 μm to about 35 μm, from about 10 μm to about 25 μm, from about 15 μm to about 45 μm, from about 15 μm to about 30 μm, from about 15 μm to about 25 μm, from about 20 μm to about 35 μm, or from about 20 μm to about 30 μm. In certain embodiments, the diameter or thickness ratio of the core and the shell are in the range of 15:85 to 85:15, 25:75 to 75:25, 30:70 to 70:30, or 40:60 to 60:40. In certain embodiments, the volume or weight ratio of the core and the shell is 95:5, 90:10, 80:20, 70:30, 60:40, 50:50, 40:60, or 30:70.

In some embodiments, the second suspension is formed by dispersing a binder material and a conductive agent in water at step 102.

Any suitable material can be used as the binder material. Some non-limiting examples include styrene-butadiene rubber (SBR), carboxymethyl cellulose (CMC), acrylonitrile copolymer, polyacrylic acid (PAA), polyacrylonitrile (PAN), LA132, LA133, LA138, latex, a salt of alginic acid, polyvinylidene fluoride (PVDF), poly(vinylidene fluoride)-hexafluoropropene (PVDF-HFP), polytetrafluoroethylene (PTFE), polystyrene, poly(vinyl alcohol) (PVA), poly(vinyl acetate), polyisoprene, polyaniline, polyethylene, polyimide, polyurethane, polyvinyl butyral, polyvinyl pyrrolidone (PVP), gelatin, chitosan, starch, agar-agar, xanthan gum, gum arabic, gellan gum, guar gum, gum karaya, tara gum, gum tragacanth, casein, amylose, pectin, carrageenans, and combinations thereof. In further embodiments, the salt of alginic acid comprises a cation selected from Na, Li, K, Ca, NH₄, Mg, Al, or a combination thereof. In certain embodiments, the binder material is free of styrene-butadiene rubber, carboxymethyl cellulose, acrylonitrile copolymer, polyacrylic acid, polyacrylonitrile, LA132, LA133, LA138, latex, a salt of alginic acid, polyvinylidene fluoride, poly(vinylidene fluoride)-hexafluoropropene, polytetrafluoroethylene, polystyrene, poly(vinyl alcohol), poly(vinyl acetate), polyisoprene, polyaniline, polyethylene, polyimide, polyurethane, polyvinyl butyral, polyvinyl pyrrolidone, gelatin, chitosan, starch, agar-agar, xanthan gum, gum arabic, gellan gum, guar gum, gum karaya, tara gum, gum tragacanth, casein, amylose, pectin or carrageenans. In certain embodiments, the binder material is not a fluorine-containing polymer such as PVDF, PVDF-HFP or PTFE.

Any suitable material can be used as the conductive agent. In some embodiments, the conductive agent is a carbonaceous material. Some non-limiting examples include carbon, carbon black, graphite, expanded graphite, graphene, graphene nanoplatelets, carbon fibers, carbon nano-fibers, graphitized carbon flake, carbon tubes, carbon nanotubes, activated carbon, mesoporous carbon, and combinations thereof. In certain embodiments, the conductive agent does not comprise a carbonaceous material.

In some embodiments, the conductive agent is a conductive polymer selected from the group consisting of polypyrrole, polyaniline, polyacetylene, polyphenylene sulfide (PPS), polyphenylene vinylene (PPV), poly(3,4-ethylenedioxythiophene) (PEDOT), polythiophene and combinations thereof. In some embodiments, the conductive agent plays two roles simultaneously not only as a conductive agent but also as a binder. In certain embodiments, the positive electrode layer comprises two components, the cathode active material and conductive polymer. In other embodiments, the positive electrode layer comprises the cathode active material, conductive agent and conductive polymer. In certain embodiments, the conductive polymer is an additive and the positive electrode layer comprises the cathode active material, conductive agent, binder and conductive polymer. In other embodiments, the positive electrode layer does not comprise a conductive polymer.

In certain embodiments, the amount of each of the binder material and the conductive material in the second suspension is independently from about 1% to about 20%, from about 1% to about 15%, from about 1% to about 10%, from about 1% to about 5%, from about 3% to about 20%, from about 5% to about 20%, from about 5% to about 10%, from about 10% to about 20%, from about 10% to about 15%, or from about 15% to about 20% by weight, based on the total weight of the second suspension. In some embodiments, the amount of each of the binder material and the conductive material in the second suspension is independently less than 20%, less than 15%, less than 10%, less than 8%, or less than 6% by weight, based on the total weight of the second suspension.

In some embodiments, the solid content of the second suspension is from about 10% to about 25%, from about 10% to about 20%, from about 10% to about 18%, from about 12% to about 25%, from about 12% to about 20%, from about 12% to about 18%, from about 15% to about 25%, from about 15% to about 20%, or from about 18% to 25% by weight, based on the total weight of the second suspension. In certain embodiments, the solid content of the second suspension is about 10%, about 12%, about 15%, about 18%, about 20%, or about 25% by weight, based on the total weight of the second suspension. In certain embodiments, the solid content of the second suspension is at least 10%, at least 12%, at least 15%, at least 18%, or at least 20% by weight, based on the total weight of the second suspension. In certain embodiments, the solid content of the second suspension is less than less than 25%, less than 20%, less than 18%, or less than 15% by weight, based on the total weight of the second suspension.

In some embodiments, the second suspension is mixed at a temperature from about 10° C. to about 40° C., from about 10° C. to about 35° C., from about 10° C. to about 30° C., from about 10° C. to about 25° C., from about 10° C. to about 20° C., or from about 10° C. to about 15° C. In some embodiments, the second suspension is mixed at a temperature of less than 40° C., less than 35° C., less than 30° C., less than 25° C., less than 20° C., less than 15° C., or less than 10° C. In some embodiments, the second suspension is mixed at a temperature of about 40° C., about 35° C., about 30° C., about 25° C., about 20° C., about 15° C., or about 10° C.

Mixing the binder material and conductive agent in the second suspension can be done while the cathode active material is being treated in the first suspension. This is advantageous as it allows quicker processing and better dispersion of materials in the third suspension. However, this is by no means required. In certain embodiments, the binder material and conductive agent are not mixed separately as a second suspension, but directly added in the first suspension and then homogenized by a homogenizer to obtain a homogenized cathode slurry. In some embodiments, the binder material and conductive agent are simultaneously or sequentially added to the first suspension already containing the cathode active material after treating the cathode active material, wherein the concentration of the base in the first suspension can be adjusted to the desired concentration of the base in the third suspension before or after adding the binder material and conductive agent. When adding the binder material and conductive agent sequentially without forming the second suspension, stirring or dispersion may be employed between the additions.

In some embodiments, the third suspension is formed by mixing the first suspension with the second suspension at step 103.

In some embodiments, the concentration of the base in the third suspension is from about 0.25% to about 3.5%, from about 0.25% to about 3.0%, from about 0.25% to about 2.5%, from about 0.25% to about 2.0%, from about 0.25% to about 1.75%, from about 0.25% to about 1.6%, from about 0.25% to about 1.5%, from about 0.25% to about 1.25%, from about 0.25% to about 1%, from about 0.3% to about 1.75%, from about 0.3% to about 1.6%, from about 0.3% to about 1.5%, from about 0.3% to about 1.25%, from about 0.3% to about 1%, from about 0.5% to about 2.5%, from about 0.5% to about 2.0%, from about 0.5% to about 1.75%, from about 0.5% to about 1.6%, from about 0.5% to about 1.5%, from about 0.5% to about 1.25%, from about 0.75% to about 2.5%, from about 0.75% to about 2.0%, from about 0.75% to about 1.75%, from about 0.75% to about 1.6%, or from about 0.75% to about 1.5% by weight, based on the total weight of the third suspension. In some embodiments, the concentration of the base in the third suspension is more than 0.25%, more than 0.3%, more than 0.5%, more than 0.75%, more than 1.0%, more than 1.25%, more than 1.5%, more than 1.6%, more than 1.8%, more than 2.0%, or more than 2.5% by weight, based on the total weight of the third suspension. In some embodiments, the concentration of the base in the third suspension is less than 3.5%, less than 3.0%, less than 2.5%, less than 2.0%, less than 1.75%, less than 1.6%, less than 1.5%, less than 1.25%, less than 1%, less than 0.75%, or less than 0.5% by weight, based on the total weight of the third suspension. In some embodiments, the concentration of the base in the third suspension is about 0.25%, about 0.3%, about 0.5%, about 0.75%, about 1.0%, about 1.25%, about 1.5%, about 1.6%, about 2.0%, about 2.5%, about 3.0%, or about 3.5% by weight, based on the total weight of the third suspension. The concentration of the base in the third suspension is equal to the concentration of the base in the homogenized cathode slurry.

In some embodiments, before homogenization of the third suspension, the third suspension is degassed under a reduced pressure for a short period of time to remove air bubbles trapped in the suspension. In some embodiments, the third suspension is degassed at a pressure from about 1 kPa to about 20 kPa, from about 1 kPa to about 15 kPa, from about 1 kPa to about 10 kPa, from about 5 kPa to about 20 kPa, from about 5 kPa to about 15 kPa, or from about 10 kPa to about 20 kPa. In certain embodiments, the suspension is degassed at a pressure less than 20 kPa, less than 15 kPa, or less than 10 kPa. In some embodiments, the suspension is degassed for a time period from about 30 minutes to about 4 hours, from about 1 hour to about 4 hours, from about 2 hours to about 4 hours, or from about 30 minutes to about 2 hours. In certain embodiments, the third suspension is degassed for a time period less than 4 hours, less than 2 hours, or less than 1 hour.

In certain embodiments, the third suspension is degassed after homogenization. The homogenized third suspension may also be degassed at the pressures and for the time durations stated in the step of degassing the third suspension before homogenization.

At step 103, the third suspension is homogenized by a homogenizer at a temperature from about 10° C. to about 30° C. to obtain a cathode slurry. The homogenizer may be equipped with a temperature control system and the temperature of the third suspension can be controlled by the temperature control system. Any homogenizer that can reduce or eliminate particle aggregation, and/or promote homogeneous distribution of slurry ingredients can be used herein. Homogeneous distribution plays an important role in fabricating batteries with good battery performance. In some embodiments, the homogenizer is a planetary stirring mixer, a stirring mixer, a blender, or an ultrasonicator.

In some embodiments, the third suspension is homogenized at a temperature from about 10° C. to about 30° C., from about 10° C. to about 25° C., from about 10° C. to about 20° C., or from about 10° C. to about 15° C. In some embodiments, the third suspension is homogenized at a temperature of less than 30° C., less than 25° C., less than 20° C., or less than 15° C.

In some embodiments, the planetary stirring mixer comprises at least one planetary blade and at least one high-speed dispersion blade. In certain embodiments, the rotational speed of the planetary blade is from about 20 rpm to about 200 rpm, from about 20 rpm to about 150 rpm, from about 30 rpm to about 150 rpm, or from about 50 rpm to about 100 rpm. In certain embodiments, the rotational speed of the dispersion blade is from about 1,000 rpm to about 4,000 rpm, from about 1,000 rpm to about 3,500 rpm, from about 1,000 rpm to about 3,000 rpm, from about 1,000 rpm to about 2,000 rpm, from about 1,500 rpm to about 3,000 rpm, or from about 1,500 rpm to about 2,500 rpm.

When the cathode active material is homogenized in an aqueous slurry for a long period of time, water can damage the cathode active material even under the presence of the base in the third suspension. In some embodiments, the third suspension is homogenized for a time period from about 10 minutes to about 6 hours, from about 10 minutes to about 5 hours, from about 10 minutes to about 4 hours, from about 10 minutes to about 3 hours, from about 10 minutes to about 2 hours, from about 10 minutes to about 1 hour, from about 10 minutes to about 30 minutes, from about 30 minutes to about 3 hours, from about 30 minutes to about 2 hours, from about 30 minutes to about 1 hour, from about 1 hour to about 6 hours, from about 1 hour to about 5 hours, from about 1 hour to about 4 hours, from about 1 hour to about 3 hours, from about 1 hour to about 2 hours, from about 2 hours to about 6 hours, from about 2 hours to about 4 hours, from about 2 hours to about 3 hours, from about 3 hours to about 5 hours, or from about 4 hours to about 6 hours. In certain embodiments, the third suspension is homogenized for a time period less than 6 hours, less than 5 hours, less than 4 hours, less than 3 hours, less than 2 hours, less than 1 hour, or less than 30 minutes. In some embodiments, the third suspension is homogenized for a time period of more than about 6 hours, more than about 5 hours, more than about 4 hours, more than about 3 hours, more than about 2 hours, more than about 1 hour, more than about 30 minutes, more than about 20 minutes, or more than about 10 minutes.

The most common method for achieving homogeneity is to use a high stirring rate, ideally inducing a turbulent flow. However, an increase in stirring rate usually leads to a huge increase in energy demand and the stresses required to achieve turbulent flow often exceed equipment capabilities. Moreover, such stresses can damage the cathode active material because some cathode active materials are shear-sensitive. An advantage of this invention is that the addition of the base stabilizes the pH of the slurry, which in turn stabilizes the viscosity of the slurry. This makes it easier to homogenize the slurry and results in efficient mixing under gentle stirring conditions. Another advantage of this invention is the reduction in the time required for the admixed components to reach homogeneity.

When the pH value of the slurry varies during homogenization and is outside of certain ranges, it may affect dispersion homogeneity and particle size distribution of the water-insoluble components, e.g., electrode active material and conductive agent in the slurry, thereby resulting in poor electrode performance. Accordingly, it is desirable to maintain a constant pH in the slurry during homogenization.

In some embodiments, the pH of the homogenized cathode slurry is from about 8 to about 14, from about 8 to about 13.5, from about 8 to about 13, from about 8 to about 12.5, from about 8 to about 12, from about 8 to about 11.5, from about 8 to about 11, from about 8 to about 10.5, from about 8 to about 10, from about 8 to about 9, from about 9 to about 14, from about 9 to about 13, from about 9 to about 12, from about 9 to about 11, from about 10 to about 14, from about 10 to about 13, from about 10 to about 12, from about 10 to about 11, from about 10.5 to about 14, from about 10.5 to about 13.5, from about 10.5 to about 13, from about 10.5 to about 12.5, from about 10.5 to about 12, from about 10.5 to about 11.5, from about 11 to about 14, from about 11 to about 13, from about 11 to about 12, from about 11.5 to about 12.5, from about 11.5 to about 12, or from about 12 to about 14. In certain embodiments, the pH of the homogenized cathode slurry is less than 14, less than 13.5, less than 13, less than 12.5, less than 12, less than 11.5, less than 11, less than 10.5, less than 10, less than 9.5, less than 9, less than 8.5, or less than 8. In some embodiments, the pH of the homogenized cathode slurry is about 7, about 7.5, about 8, about 8.5, about 9, about 9.5, about 10, about 10.5, about 11, about 11.5, about 12, about 12.5, about 13, about 13.5 or about 14.

In certain embodiments, the amount of the conductive agent in the homogenized cathode slurry is from about 0.5% to about 5%, from about 0.5% to about 3%, from about 1% to about 5%, from about 1% to about 4%, or from about 2% to about 3% by weight, based on the total weight of the homogenized cathode slurry.

In some embodiments, the amount of the conductive agent in the homogenized cathode slurry is at least about 0.5%, at least about 1%, at least about 2%, at least about 3%, or at least about 4% by weight, based on the total weight of the homogenized cathode slurry. In certain embodiments, the amount of the conductive agent in the homogenized cathode slurry is at most about 1%, at most about 2%, at most about 3%, at most about 4%, or at most about 5% by weight, based on the total weight of the homogenized cathode slurry.

In certain embodiments, the amount of the binder material in the homogenized cathode slurry is from about 1% to about 15%, from about 1% to about 10%, from about 1% to about 5%, from about 3% to about 15%, from about 5% to about 15%, from about 5% to about 10%, or from about 10% to about 15% by weight, based on the total weight of the homogenized cathode slurry. In some embodiments, the amount of the binder material in the homogenized cathode slurry is less than 15%, less than 10%, less than 8%, or less than 6% by weight, based on the total weight of the homogenized cathode slurry.

In some embodiments, the weight of the binder material is greater than, smaller than, or equal to the weight of the conductive agent in the homogenized cathode slurry. In certain embodiments, the ratio of the weight of the binder material to the weight of the conductive agent is from about 1:10 to about 10:1, from about 1:10 to about 5:1, from about 1:10 to about 1:1, from about 1:10 to about 1:5, from about 1:5 to about 5:1, from about 1:3 to about 3:1, from about 1:2 to about 2:1, or from about 1:1.5 to about 1.5:1.

In some embodiments, the solid content of the homogenized cathode slurry is from about 40% to about 80%, from about 45% to about 75%, from about 45% to about 70%, from about 45% to about 65%, from about 45% to about 60%, from about 45% to about 55%, from about 45% to about 50%, from about 50% to about 75%, from about 50% to about 70%, from about 50% to about 65%, from about 55% to about 75%, from about 55% to about 70%, from about 60% to about 75%, or from about 65% to about 75% by weight, based on the total weight of the homogenized cathode slurry. In certain embodiments, the solid content of the homogenized cathode slurry is about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, about 70%, about 75%, or about 80% by weight, based on the total weight of the homogenized cathode slurry. In certain embodiments, the solid content of the homogenized cathode slurry is at least 40%, at least 45%, at least 50%, at least 55%, at least 60%, at least 65%, or at least 70% by weight, based on the total weight of the homogenized cathode slurry. In certain embodiments, the solid content of the homogenized cathode slurry is less than 75%, less than 70%, less than 65%, less than 60%, less than 55%, or less than 50% by weight, based on the total weight of the homogenized cathode slurry.

The homogenized cathode slurry of the present invention can have a higher solid content than conventional cathode active material slurries. This allows more cathode active material to be prepared for further processing at any one time, thus improving efficiency and maximizing productivity.

High viscosity of the slurry makes it difficult to disperse the bulk materials to obtain a uniform slurry. The solvent used in the homogenized cathode slurry disclosed herein can comprise at least one alcohol. The addition of the alcohol can improve the processability of the slurry and lower the freezing point of water. Some non-limiting examples of suitable alcohol include ethanol, isopropanol, n-propanol, tert-butanol, n-butanol, and combinations thereof. The total amount of the alcohol can range from about 1% to about 30%, from about 1% to about 20%, from about 1% to about 10%, from about 1% to about 5%, from about 1% to about 3%, from about 3% to about 30%, from about 3% to about 20%, from about 3% to about 10%, from about 5% to about 20%, from about 5% to about 15%, from about 5% to about 10%, or from about 8% to about 15% by weight, based on the total weight of the homogenized cathode slurry. In some embodiments, the slurry does not comprise an alcohol.

The viscosity of the homogenized cathode slurry is preferably less than about 8,000 mPa·s. In some embodiments, the viscosity of the homogenized cathode slurry is from about 1,000 mPa·s to about 8,000 mPa·s, from about 1,000 mPa·s to about 7,000 mPa·s, from about 1,000 mPa·s to about 6,000 mPa·s, from about 1,000 mPa·s to about 5,000 mPa·s, from about 1,000 mPa·s to about 4,000 mPa·s, from about 1,000 mPa·s to about 3,000 mPa·s, from about 1,000 mPa·s to about 2,500 mPa·s, or from about 1,000 mPa·s to about 2,000 mPa s. In certain embodiments, the viscosity of the homogenized cathode slurry is less than 8,000 mPa·s, less than 7,000 mPa·s, less than 6,000 mPa·s, less than 5,000 mPa·s, less than 4,000 mPa·s, less than 3,000 mPa·s, less than 2,500 mPa·s, less than 2,000 mPa·s, less than 1,500 mPa·s, or less than 1,000 mPa·s. In some embodiments, the viscosity of the homogenized cathode slurry is about 1,000 mPa·s, about 2,000 mPa·s, about 3,000 mPa·s, about 4,000 mPa·s, about 5,000 mPa·s, about 6,000 mPa·s, about 7,000 mPa·s, or about 8,000 mPa·s. Thus, the resultant slurry can be fully mixed or homogeneous.

At an alkaline pH, surface chemistry of the cathode active material may change, thereby affecting dispersion homogeneity and particle size distribution of the electrode components (e.g., the cathode active material and conductive agent) in the cathode slurry.

The cathode slurry disclosed herein has a small D50, and a uniform and narrow particle size distribution. FIG. 2 depicts the D50 size of cathode active material particles in an NMP-based slurry and a base-treated slurry of the present invention respectively. It can be seen that the D50 of the NMP-based slurry is rather large and fluctuates significantly, while the D50 of the base-treated slurry remains small and constant over time. This shows that the particles of the base-treated slurry of the present invention do not agglomerate or break apart over time, so the slurry maintains a high and stable level of dispersion even after a long period of storage. This not only improves the lifespan of the lithium-ion batteries made therefrom, but also improves production efficiency as slurries can be used long after being prepared without fear of any changes in the dispersion of the slurry particles.

In some embodiments, the cathode slurry of the present invention has a particle size D50 in the range from about 1 μm to about 20 μm, from about 1 μm to about 18 μm, from about 1 μm to about 15 μm, from about 1 μm to about 12 μm, from about 1 μm to about 10 μm, from about 1 μm to about 8 μm, from about 1 μm to about 6 μm, from about 3 μm to about 20 μm, from about 3 μm to about 18 μm, from about 3 μm to about 15 μm, from about 3 μm to about 12 μm, from about 3 μm to about 10 μm, from about 3 μm to about 8 μm, from about 3 μm to about 6 μm, from about 4 μm to about 15 μm, from about 4 μm to about 12 μm, from about 4 μm to about 10 μm, from about 4 μm to about 8 μm, from about 4 μm to about 6 μm, from about 6 μm to about 20 μm, from about 6 μm to about 18 μm, from about 6 μm to about 15 μm, from about 6 μm to about 12 μm, from about 6 μm to about 10 μm, from about 6 μm to about 8 μm, from about 6 μm to about 15 μm, from about 8 μm to about 15 μm, from about 8 μm to about 12 μm, from about 8 μm to about 10 μm, from about 10 μm to about 20 μm, from about 10 μm to about 18 μm, from about 10 μm to about 15 μm, from about 10 μm to about 12 μm, from about 11 μm to about 20 μm, from about 11 μm to about 18 μm, or from about 11 μm to about 15 μm. In certain embodiments, the particle diameter D50 of the cathode active material is less than 20 μm, less than 18 μm, less than 15 μm, less than 12 μm, less than 10 μm, less than 8 μm, less than 7 μm, less than 6 μm, less than 5 μm, less than 4 μm or less than 3 μm. In some embodiments, the particle diameter D50 of the cathode active material is greater than 1 μm, greater than 2 μm, greater than 3 μm, greater than 4 μm, greater than 5 μm, greater than 6 μm, greater than 8 μm, greater than 10 μm, or greater than 11 μm.

In conventional methods of preparing cathode slurry, a dispersing agent may be used to assist in dispersing the cathode active material, conductive agent and binder material in the slurry. Some non-limiting examples of the dispersing agent include a polymeric acid and a surfactant that can lower the surface tension between a liquid and a solid. In some embodiments, the dispersing agent is a nonionic surfactant, an anionic surfactant, a cationic surfactant, an amphoteric surfactant, or a combination thereof.

One of the advantages of the present invention is that the slurry components can be dispersed homogeneously at room temperature without the use of a dispersing agent. In some embodiments, the method of the present invention does not comprise a step of adding a dispersing agent to the first suspension, second suspension, third suspension or the homogenized cathode slurry. In certain embodiments, each of the first suspension, the second suspension, third suspension and the homogenized cathode slurry is independently free of a dispersing agent.

Some non-limiting examples of the polymeric acid include polylactic acid, polysuccinic acid, polymaleic acid, pyromucic acid, polyfumaric acid, polysorbic acid, polylinoleic acid, polylinolenic acid, polyglutamic acid, polymethacrylic acid, polylicanic acid, polyglycolic acid, polyaspartic acid, polyamic acid, polyformic acid, polyacetic acid, polypropionic acid, polybutyric acid, polysebacic acid, copolymers thereof, and combinations thereof. In certain embodiments, the homogenized cathode slurry is free of a polymeric acid.

Some non-limiting examples of suitable nonionic surfactants include a carboxylic ester, a polyethylene glycol ester, and combinations thereof.

Some non-limiting examples of suitable anionic surfactants include a salt of an alkyl sulfate, an alkyl polyethoxylate ether sulfate, an alkyl benzene sulfonate, an alkyl ether sulfate, a sulfonate, a sulfosuccinate, a sarcosinate, and combinations thereof. In some embodiments, the anionic surfactant comprises a cation selected from the group consisting of sodium, potassium, ammonium, and combinations thereof. In certain embodiments, the anionic surfactant is sodium dodecylbenzene sulfonate, sodium stearate, lithium dodecyl sulfate, or a combination thereof. In some embodiments, the homogenized cathode slurry is free of an anionic surfactant.

Some non-limiting examples of suitable cationic surfactant include an ammonium salt, a phosphonium salt, an imidazolium salt, a sulfonium salt, and combinations thereof. Some non-limiting examples of suitable ammonium salt include stearyl trimethylammonium bromide (STAB), cetyl trimethylammonium bromide (CTAB), myristyl trimethylammonium bromide (MTAB), trimethylhexadecyl ammonium chloride, and combinations thereof. In some embodiments, the homogenized cathode slurry is free of a cationic surfactant.

Some non-limiting examples of suitable amphoteric surfactant are surfactants that contain both cationic and anionic groups. The cationic group is ammonium, phosphonium, imidazolium, sulfonium, or a combination thereof. The anionic hydrophilic group is carboxylate, sulfonate, sulfate, phosphonate, or a combination thereof. In some embodiments, the homogenized cathode slurry is free of the amphoteric surfactant.

After uniform mixing of slurry components, the homogenized cathode slurry can be applied on a current collector to form a coated film on the current collector, followed by drying in step 104. The current collector acts to collect electrons generated by electrochemical reactions of the cathode active material or to supply electrons required for the electrochemical reactions. In some embodiments, the current collector can be in the form of a foil, sheet or film. In certain embodiments, the current collector is stainless steel, titanium, nickel, aluminum, copper, or alloys thereof or electrically-conductive resin. In certain embodiments, the current collector has a two-layered structure comprising an outer layer and an inner layer, wherein the outer layer comprises a conductive material and the inner layer comprises an insulating material or another conductive material; for example, aluminum mounted with a conductive resin layer or a polymeric insulating material coated with an aluminum film. In some embodiments, the current collector has a three-layered structure comprising an outer layer, a middle layer and an inner layer, wherein the outer and inner layers comprise a conductive material and the middle layer comprises an insulating material or another conductive material; for example, a plastic substrate coated with a metal film on both sides. In certain embodiments, each of the outer layer, middle layer and inner layer is independently stainless steel, titanium, nickel, aluminum, copper, or alloys thereof or electrically-conductive resin. In some embodiments, the insulating material is a polymeric material selected from the group consisting of polycarbonate, polyacrylate, polyacrylonitrile, polyester, polyamide, polystyrene, polyurethane, polyepoxy, poly(acrylonitrile butadiene styrene), polyimide, polyolefin, polyethylene, polypropylene, polyphenylene sulfide, poly(vinyl ester), polyvinyl chloride, polyether, polyphenylene oxide, cellulose polymer and combinations thereof. In certain embodiments, the current collector has more than three layers. In some embodiments, the current collector is coated with a protective coating. In certain embodiments, the protective coating comprises a carbon-containing material. In some embodiments, the current collector is not coated with a protective coating.

One undesirable reaction that occurs to a nickel-containing cathode active material in an aqueous slurry is lithium ions leaching from the surface of the cathode active material and reacting with water to form LiOH. The leaching of lithium ions causes changes in the cathode active material, resulting in reduced performance of the battery cell made therefrom. Therefore, lithium ion leaching is a major obstacle to applying water-based methods to cathode slurry preparation, especially for nickel-containing cathode active materials.

It has been discovered that by treating the cathode active material in a nitrogen-containing base helps minimize leaching of lithium ions in the cathode slurry. FIG. 3 is a graph showing the relationship between the concentration of lithium ions in the cathode slurry and time. The concentration of lithium ions measured in a slurry that has been prepared by the method disclosed herein is substantially less than that of an untreated cathode active material. The method disclosed herein improves stability of cathode active materials in aqueous slurries and effectively reduces the amount of the lithium ions leached.

In some embodiments, the lithium ion concentration in the cathode slurry is in the range from about 300 parts per million (ppm) to about 800 ppm, from about 350 ppm to about 800 ppm, from about 400 ppm to about 800 ppm, from about 500 ppm to about 800 ppm, from about 600 ppm to about 800 ppm, from about 700 ppm to about 800 ppm, from about 300 ppm to about 750 ppm, from about 300 ppm to about 700 ppm, from about 300 ppm to about 600 ppm, from about 300 ppm to about 500 ppm, from about 300 ppm to about 400 ppm, from about 300 ppm to about 350 ppm, from about 400 ppm to about 700 ppm, or from about 500 ppm to about 600 ppm, based on the total weight of the cathode slurry. In some embodiments, the lithium ion concentration in the cathode slurry is more than 300 ppm, more than 350 ppm, more than 400 ppm, more than 500 ppm, or more than 600 ppm, based on the total weight of the cathode slurry. In some embodiments, the lithium ion concentration is less than 800 ppm, less than 750 ppm, less than 700 ppm, less than 600 ppm, or less than 500 ppm, based on the total weight of the cathode slurry. In some embodiments, the lithium ion concentration in the cathode slurry is about 300 ppm, about 350 ppm, about 400 ppm, about 450 ppm, about 500 ppm, about 550 ppm, about 600 ppm, about 650 ppm, about 700 ppm, about 750 ppm, or about 800 ppm, based on the total weight of the cathode slurry.

In certain embodiments, the thickness of each of the cathode and anode electrode layers on the current collector is independently from about 10 μm to about 90 μm, from about 15 μm to about 90 μm, from about 20 μm to about 90 μm, from about 25 μm to about 90 μm, from about 25 μm to about 80 μm, from about 25 μm to about 75 μm, from about 25 μm to about 50 μm, from about 30 μm to about 90 μm, from about 30 μm to about 80 μm, from about 35 μm to about 90 μm, from about 35 μm to about 85 μm, from about 35 μm to about 80 μm, or from about 35 μm to about 75 μm. In some embodiments, the thickness of the electrode layer on the current collector is about 25 μm, about 30 μm, about 35 μm, about 40 μm, about 45 μm, about 50 μm, about 55 μm, about 60 μm, about 65 μm, about 70 μm, or about 75 μm.

In some embodiments, the surface density of each of the cathode and anode electrode layers on the current collector is independently from about 1 mg/cm² to about 40 mg/cm², from about 1 mg/cm² to about 35 mg/cm², from about 1 mg/cm² to about 30 mg/cm², from about 1 mg/cm² to about 25 mg/cm², from about 1 mg/cm² to about 15 mg/cm², from about 3 mg/cm² to about 40 mg/cm², from about 3 mg/cm² to about 35 mg/cm², from about 3 mg/cm² to about 30 mg/cm², from about 3 mg/cm² to about 25 mg/cm², from about 3 mg/cm² to about 20 mg/cm², from about 3 mg/cm² to about 15 mg/cm², from about 5 mg/cm² to about 40 mg/cm², from about 5 mg/cm² to about 35 mg/cm², from about 5 mg/cm² to about 30 mg/cm², from about 5 mg/cm² to about 25 mg/cm², from about 5 mg/cm² to about 20 mg/cm², from about 5 mg/cm² to about 15 mg/cm², from about 8 mg/cm² to about 40 mg/cm², from about 8 mg/cm² to about 35 mg/cm², from about 8 mg/cm² to about 30 mg/cm², from about 8 mg/cm² to about 25 mg/cm², from about 8 mg/cm² to about 20 mg/cm², from about 10 mg/cm² to about 40 mg/cm², from about 10 mg/cm² to about 35 mg/cm², from about 10 mg/cm² to about 30 mg/cm², from about 10 mg/cm² to about 25 mg/cm², from about 10 mg/cm² to about 20 mg/cm², from about 15 mg/cm² to about 40 mg/cm², or from about 20 mg/cm² to about 40 mg/cm².

In some embodiments, a conductive layer can be coated on an aluminum current collector to improve its current conductivity. In certain embodiments, the conductive layer comprises a material selected from the group consisting of carbon, carbon black, graphite, expanded graphite, graphene, graphene nanoplatelets, carbon fibers, carbon nano-fibers, graphitized carbon flake, carbon tubes, carbon nanotubes, activated carbon, mesoporous carbon, and combinations thereof. In some embodiments, the conductive agent is not carbon, carbon black, graphite, expanded graphite, graphene, graphene nanoplatelets, carbon fibers, carbon nano-fibers, graphitized carbon flake, carbon tubes, carbon nanotubes, activated carbon, or mesoporous carbon.

In some embodiments, the conductive layer has a thickness from about 0.5 μm to about 5.0 μm. Thickness of the conductive layer will affect the volume occupied by the current collector within a battery and the amount of the electrode material and hence the capacity in the battery.

In certain embodiments, the thickness of the conductive layer on the current collector is from about 0.5 μm to about 4.5 μm, from about 1.0 μm to about 4.0 μm, from about 1.0 μm to about 3.5 μm, from about 1.0 μm to about 3.0 μm, from about 1.0 μm to about 2.5 μm, from about 1.0 μm to about 2.0 μm, from about 1.1 μm to about 2.0 μm, from about 1.2 μm to about 2.0 μm, from about 1.5 μm to about 2.0 μm, from about 1.8 μm to about 2.0 μm, from about 1.0 μm to about 1.8 μm, from about 1.2 μm to about 1.8 μm, from about 1.5 μm to about 1.8 μm, from about 1.0 μm to about 1.5 μm, or from about 1.2 to about 1.5 μm. In some embodiments, the thickness of the conductive layer on the current collector is less than 4.5 μm, less than 4.0 μm, less than 3.5 μm, less than 3.0 μm, less than 2.5 μm, less than 2.0 μm, less than 1.8 μm, less than 1.5 μm, or less than 1.2 μm. In some embodiments, the thickness of the conductive layer on the current collector is more than 1.0 μm, more than 1.2 μm, more than 1.5 μm, more than 1.8 μm, more than 2.0 μm, more than 2.5 μm, more than 3.0 μm, or more than 3.5 μm.

FIGS. 4 a and 4 b depict the appearance of the surface of cathode electrode layers formed respectively by an untreated slurry and a base-treated slurry in accordance with the present invention. FIG. 4 a shows pinholes of different size distributed across the surface of the electrode layer, while FIG. 4 b shows a smooth, continuous electrode layer. Such pinholes lead to inferior electrochemical performance, such as lower discharge capacities and poor cycle life, compared with electrodes prepared by the present invention. The improved surface morphology of the electrode layer provided by the present invention leads to better electrochemical performance of the battery created therefrom. Battery performance data is also presented below, which shows the enhanced performance achieved when using electrodes produced in accordance with the present invention.

In addition, the cathode prepared by the present invention exhibits strong adhesion of the electrode layer to the current collector. It is important for the electrode layer to have good peeling strength to the current collector as this prevents delamination or separation of the electrode, which would greatly influence the mechanical stability of the electrodes and the cyclability of the battery. Therefore, the electrodes should have sufficient peeling strength to withstand the rigors of battery manufacture.

FIG. 5 is a bar graph showing the peeling strengths of cathodes coated respectively with an organic slurry, an aqueous slurry comprising untreated cathode active material and an aqueous slurry prepared according to the present invention. The graph shows an increase in the peeling strength of the coated film to the current collector for the electrode prepared by the method disclosed herein.

In some embodiments, the peeling strength between the current collector and the electrode layer is in the range from about 1.0 N/cm to about 3.0 N/cm, from about 1.2 N/cm to about 3.0 N/cm, from about 1.5 N/cm to about 3.0 N/cm, from about 1.8 N/cm to about 3.0 N/cm, from about 2.0 N/cm to about 3.0 N/cm, from about 2.2 N/cm to about 3.0 N/cm, from about 2.5 N/cm to about 3.0 N/cm, from about 1.0 N/cm to about 2.5 N/cm, from about 1.2 N/cm to about 2.5 N/cm, from about 1.5 N/cm to about 2.5 N/cm, from about 1.8 N/cm to about 2.5 N/cm, from about 2.0 N/cm to about 2.5 N/cm, from about 1.0 N/cm to about 2.0 N/cm, from about 1.2 N/cm to about 2.0 N/cm, or from about 1.5 N/cm to about 2.0 N/cm. In some embodiments, the peeling strength between the current collector and the electrode layer is 1.0 N/cm or more, 1.2 N/cm or more, 1.5 N/cm or more, 2.0 N/cm or more, 2.2 N/cm or more, or 2.5 N/cm or more. In some embodiments the peeling strength between the current collector and the electrode layer is less than 3.0 N/cm, less than 2.8 N/cm, less than 2.5 N/cm, less than 2.2 N/cm, less than 2.0 N/cm, less than 1.8 N/cm, or less than 1.5 N/cm.

Table 4 below shows ICP mass spectroscopy data of diluted slurries of NMC811 that was pre-treated with ammonia at various concentrations. The data demonstrates that less lithium from the cathode active material is dissolved in the solvent when the cathode active material is pre-treated, thus showing that the pre-treatment of the present invention can inhibit loss of lithium from the cathode active material. It can be seen that the inhibition of lithium loss of the cathode active material is correlated with the concentration of the ammonia used.

In some embodiments, the lithium loss of the cathode active material is inhibited by a percentage between about 1 percent and about 50 percent, relative to the lithium loss of the cathode material in pure water. In certain embodiments, the lithium loss of the cathode active material is inhibited by a percentage between about 5 percent and about 50 percent, between about 10 percent and about 50 percent, between about 15 percent and about 50 percent, between about 20 percent and about 50 percent, between about 25 percent and about 50 percent, between about 1 percent and about 45 percent, between about 5 percent and about 45 percent, between about 10 percent and about 45 percent, between about 15 percent and about 45 percent, between about 20 percent and about 45 percent, between about 25 percent and about 45 percent, between about 1 percent and about 40 percent, between about 5 percent and about 40 percent, between about 10 percent and about 40 percent, between about 15 percent about and 40 percent, between about 20 percent and about 40 percent, between about 1 percent and about 35 percent, between about 5 percent and about 35 percent, between about 10 percent and about 35 percent, between about 15 percent and about 35 percent, between about 20 percent and about 35 percent, between about 1 percent and about 30 percent, between about 5 percent and about 30 percent, between about 10 percent and about 30 percent, between about 15 percent and about 30 percent, between about 1 percent and about 20 percent, between about 3 percent and about 20 percent, between about 5 percent and about 20 percent, between about 8 percent and about 20 percent, between about 10 percent and about 20 percent, between about 1 percent and about 15 percent, or about between 1 percent and about 10 percent, relative to the lithium loss of the cathode active material in pure water. In some embodiments, the lithium loss of the cathode active material is inhibited by a percentage of about 1 percent or above, about 3 percent or above, about 5 percent or above, about 8 percent or above, about 10 percent or above, about 12 percent or above, about 15 percent or above, about 18 percent or above, about 20 percent or above, about 25 percent or above, or about 30 percent or above, relative to the lithium loss of the cathode active material in pure water. In some embodiments, the lithium loss of the cathode active material is inhibited by a percentage of about 50 percent or below, about 45 percent or below, about 40 percent or below, about 35 percent or below, about 30 percent or below, about 25 percent or below, about 20 percent or below, about 15 percent or below, about 10 percent or below, or about 5 percent or below, relative to the lithium loss of the cathode active material in pure water.

During coating, pH is a very important parameter in controlling the slurry's stability as it affects key properties of the slurry, such as viscosity and degree of dispersion. If the slurry pH changes, then such key properties will also change. The risk of pH instability causes a need to coat the slurry on the current collector immediately after homogenization. This is very difficult to realize under mass production conditions, where the coating processes often continue for many hours. Any fluctuations in the key properties during coating are a severe issue and will make the coating process unstable. One benefit of the present invention is that the slurry pH, and thus the key properties, remain stable during homogenization and also for a long time after homogenization. It is found that the pH of the slurry disclosed herein remains relatively constant during extended stagnant storage of up to two weeks, while the pH of conventional water-based slurries rises significantly during storage. The stability of the pH allows the slurry disclosed herein to remain homogenous and uniform during such extended storage, allowing sufficient time for transportation of the slurry to proceed to the coating process.

The cathode slurry can be obtained by homogenizing the third suspension for a time period from about 10 minutes to about 6 hours, from about 1 hour to about 6 hours, from about 2 hours to about 6 hours, from about 4 hours to about 6 hours, from about 10 minutes to about 5 hours, from about 1 hour to about 5 hours, from about 3 hours to about 5 hours, from about 10 minutes to about 4 hours, from about 1 hour to about 4 hours, from about 2 hours to about 4 hours, from about 10 minutes to about 3 hours, from about 1 hour to about 3 hours, from about 2 hours to about 3 hours, from about 10 minutes to about 2 hours, from about 30 minutes to about 2 hours, from about 1 hour to about 2 hours, from about 10 minutes to about 1 hour, from about 30 minutes to about 1 hour, or from about 10 minutes to about 30 minutes.

In some embodiments, the concentration of the base in the cathode slurry is from about 0.5% to about 3.5%, from about 0.5% to about 3.0%, from about 0.5% to about 2.5%, from about 0.5% to about 2.0%, from about 0.5% to about 1.75%, from about 0.5% to about 1.6%, from about 0.5% to about 1.5%, or from about 0.5% to about 1.25%, based on the total weight of the cathode slurry.

In some embodiments, the amount of the cathode active material is from about 10% to about 80%, from about 10% to about 70%, from about 10% to about 60%, from about 10% to about 50%, from about 10% to about 40%, from about 10% to about 30%, from about 10% to about 20%, from about 25% to about 80%, from about 25% to about 70%, from about 25% to about 60%, from about 25% to about 50%, from about 25% to about 40%, from about 30% to about 70%, from about 30% to about 60%, from about 30% to about 50%, from about 30% to about 40%, from about 40% to about 80%, from about 35% to about 65%, from about 35% to about 50%, from about 35% to about 45%, from about 40% to about 70%, from about 40% to about 60%, from about 40% to about 50%, from about 45% to about 80%, from about 45% to about 70%, from about 45% to about 60%, from about 45% to about 50%, from about 50% to about 80%, from about 50% to about 70%, from about 50% to about 60%, from about 60% to about 80%, or from about 60% to about 70%, by weight or volume, based on the total weight or volume of the cathode slurry. In certain embodiments, the amount of the cathode active material is at least 10%, at least 15%, at least 20%, at least 25%, at least 27.5%, at least 30%, at least 32.5%, at least 35%, at least 37.5%, at least 40%, at least 42.5%, at least 45%, at least 47.5%, at least 50%, at least 52.5%, at least 55%, at least 57.5, at least 60%, at least 65%, at least 70%, or at least 75% by weight or volume, based on the total weight or volume of the cathode slurry. In certain embodiments, the amount of the cathode active material is at most 25%, at most 27.5%, at most 30%, at most 32.5%, at most 35%, at most 37.5%, at most 40%, at most 42.5%, at most 45%, at most 47.5%, at most 50%, at most 52.5%, at most 55%, at most 57.5%, at most 60%, at most 65%, at most 70%, or at most 75% by weight or volume, based on the total weight or volume of the cathode slurry.

The slurry should maintain a stable pH during homogenization, as an unstable pH can significantly reduce the lifetime of the battery. In general, when the cathode active material is pre-treated in a base, the slurry pH was found to decrease slightly during homogenization. In certain embodiments, the decrease in pH observed during homogenization is from about 0.1 pH units to about 1.0 pH unit, from about 0.1 pH units to about 0.8 pH units, from about 0.1 pH units to about 0.6 pH units, from about 0.1 pH units to about 0.5 pH units, from about 0.1 pH units to about 0.4 pH units, or from about 0.1 pH units to about 0.3 pH units. In certain embodiments, the decrease in pH observed during homogenization is less than 1.0 pH unit, less than 0.8 pH units, less than 0.6 pH units, less than 0.5 pH units, less than 0.45 pH units, less than 0.4 pH units, less than 0.35 pH units, less than 0.3 pH units, less than 0.2 pH units, or less than 0.1 pH units.

The thickness of the current collector affects the volume it occupies within the battery, the amount of the electrode active material needed, and hence the capacity in the battery. In some embodiments, the current collector has a thickness from about 5 μm to about 30 μm. In certain embodiments, the current collector has a thickness from about 5 μm to about 20 μm, from about 5 μm to about 15 μm, from about 10 μm to about 30 μm, from about 10 μm to about 25 μm, or from about 10 μm to about 20 μm.

In certain embodiments, the coating process is performed using a doctor blade coater, a slot-die coater, a transfer coater, a spray coater, a roll coater, a gravure coater, a dip coater, or a curtain coater.

Evaporating the solvent to create a dry porous electrode is needed to fabricate the battery. After applying the homogenized cathode slurry on a current collector, the coated film on the current collector can be dried by a dryer to obtain the battery electrode. Any dryer that can dry the coated film on the current collector can be used herein. Some non-limiting examples of the dryer include a batch drying oven, a conveyor drying oven, and a microwave drying oven. Some non-limiting examples of the conveyor drying oven include a conveyor hot air drying oven, a conveyor resistance drying oven, a conveyor inductive drying oven, and a conveyor microwave drying oven.

In some embodiments, the conveyor drying oven for drying the coated film on the current collector includes one or more heating sections, wherein each of the heating sections is individually temperature-controlled, and wherein each of the heating sections may include independently controlled heating zones.

In certain embodiments, the conveyor drying oven comprises a first heating section positioned on one side of the conveyor and a second heating section positioned on an opposing side of the conveyor from the first heating section, wherein each of the first and second heating sections independently comprises one or more heating elements and a temperature control system connected to the heating elements of the first heating section and the second heating section in a manner to monitor and selectively control the temperature of each heating section.

In some embodiments, the conveyor drying oven comprises a plurality of heating sections, wherein each heating section includes independent heating elements that are operated to maintain a constant temperature within the heating section.

In certain embodiments, each of the first and second heating sections independently has an inlet heating zone and an outlet heating zone, wherein each of the inlet and outlet heating zones independently comprises one or more heating elements and a temperature control system connected to the heating elements of the inlet heating zone and the outlet heating zone in a manner to monitor and selectively control the temperature of each heating zone separately from the temperature control of the other heating zones.

The coated film on the current collector should be dried at a temperature of approximately 75° C. or less in approximately 20 minutes or less. Drying the coated positive electrode at temperatures above 75° C. may result in undesirable deformation of the cathode, thus affecting the performance of the positive electrode.

In some embodiments, the coated film on the current collector can be dried at a temperature from about 25° C. to about 75° C. In certain embodiments, the coated film on the current collector can be dried at a temperature from about 25° C. to about 70° C., from about 25° C. to about 65° C., about 25° C. to about 60° C., about 25° C. to about 55° C., about 25° C. to about 50° C., about 25° C. to about 45° C., about 25° C. to about 40° C., from about 30° C. to about 75° C., from about 30° C. to about 70° C., from about 30° C. to about 65° C., from about 30° C. to about 60° C., from about 30° C. to about 55° C., from about 30° C. to about 50° C., from about 35° C. to about 75° C., from about 35° C. to about 70° C., from about 35° C. to about 65° C., from about 35° C. to about 60° C., from about 40° C. to about 75° C., from about 40° C. to about 70° C., from about 40° C. to about 65° C., or from about 40° C. to about 60° C. In some embodiments, the coated film on the current collector is dried at a temperature less than 75° C., less than 70° C., less than 65° C., less than 60° C., less than 55° C., or less than 50° C. In some embodiments, the coated film on the current collector is dried at a temperature of higher than about 70° C., higher than about 65° C., higher than about 60° C., higher than about 55° C., higher than about 50° C., higher than about 45° C., higher than about 40° C., or higher than about 35° C., higher than about 30° C., or higher than about 25° C.

In certain embodiments, the conveyor moves at a speed from about 1 meter/minute to about 120 meters/minute, from about 1 meter/minute to about 100 meters/minute, from about 1 meter/minute to about 80 meters/minute, from about 1 meter/minute to about 60 meters/minute, from about 1 meter/minute to about 40 meters/minute, from about 10 meters/minute to about 120 meters/minute, from about 10 meters/minute to about 80 meters/minute, from about 10 meters/minute to about 60 meters/minute, from about 10 meters/minute to about 40 meters/minute, from about 25 meters/minute to about 120 meters/minute, from about 25 meters/minute to about 100 meters/minute, from about 25 meters/minute to about 80 meters/minute, from about 25 meters/minute to about 60 meters/minute, from about 50 meters/minute to about 120 meters/minute, from about 50 meters/minute to about 100 meters/minute, from about 50 meters/minute to about 80 meters/minute, from about 75 meters/minute to about 120 meters/minute, from about 75 meters/minute to about 100 meters/minute, from about 2 meters/minute to about 25 meters/minute, from about 2 meters/minute to about 20 meters/minute, from about 2 meters/minute to about 16 meters/minute, from about 3 meters/minute to about 30 meters/minute, from about 3 meters/minute to about 20 meters/minute, or from about 3 meters/minute to about 16 meters/minute.

Controlling the conveyor length and speed can regulate the drying time of the coated film. In some embodiments, the coated film on the current collector can be dried for a time period from about 2 minutes to about 20 minutes, from about 2 minutes to about 17 minutes, from about 2 minutes to about 15 minutes, from about 2 minutes to about 14 minutes, from about 2 minutes to about 10 minutes, from about 2 minutes to about 11 minutes, from about 2 minutes to about 8 minutes, from about 5 minutes to about 20 minutes, from about 5 minutes to about 11 minutes, from about 5 minutes to about 14 minutes, from about 5 minutes to about 17 minutes, or from about 5 minutes to about 10 minutes. In certain embodiments, the coated film on the current collector can be dried for a time period of less than 5 minutes, less than 8 minutes, less than 10 minutes, less than 11 minutes, less than 14 minutes, less than 17 minutes, or less than 20 minutes. In some embodiments, the coated film on the current collector can be dried for a time period of about 5 minutes, about 8 minutes, about 10 minutes, about 11 minutes, about 14 minutes, about 17 minutes, or about 20 minutes.

The method disclosed herein has the advantage that aqueous solvents can be used in the manufacturing process, which can save on processing time and equipment, as well as improve safety by eliminating the need to handle or recycle hazardous organic solvents. Since aqueous solvents are used in the present invention, the electrode would require less time and energy to dry. In addition, costs are reduced by simplifying the overall process. Therefore, this method is especially suited for industrial processes because of its low cost and ease of handling.

As described above, by treating the cathode active material with the base disclosed herein, the slurry preparation method disclosed herein has a controlled cathode slurry pH, favorably enhancing the slurry's stability. The development of water-based cathode slurries without lowering the battery performance such as cyclability and capacity is achieved by the present invention. Batteries comprising positive electrodes prepared in accordance with the present invention show high cycle stability. In addition, the low drying temperatures and decreased drying times of the coated film significantly improve performance of the batteries.

The electrode assembly comprises at least one cathode, at least one anode and at least one separator placed in between the cathode and anode. Also provided herein is an electrode assembly comprising a cathode prepared by the method described above.

In certain embodiments, the electrode assembly is dried after being assembled to reduce its water content. In other embodiments, at least one of the components of the electrode assembly is dried before the electrode assembly is assembled. In some embodiments, at least one of the components is pre-dried before assembly of the electrode assembly. In certain embodiments, the separator is pre-dried before being assembled to the electrode assembly.

It is not necessary to dry the separator to a very low water content. The remaining water content of the pre-dried separator can be further reduced by the subsequent drying step. In some embodiments, the water content in the pre-dried separator is from about 50 ppm to about 800 ppm, from about 50 ppm to about 700 ppm, from about 50 ppm to about 600 ppm, from about 50 ppm to about 500 ppm, from about 50 ppm to 400 ppm, from about 50 ppm to about 300 ppm, from about 50 ppm to 200 ppm, from about 50 ppm to 100 ppm, from about 100 ppm to about 500 ppm, from about 100 ppm to about 400 ppm, from about 100 ppm to about 300 ppm, from about 100 ppm to about 200 ppm, from about 200 ppm to about 500 ppm, from about 200 ppm to about 400 ppm, from about 300 ppm to about 800 ppm, from about 300 ppm to about 600 ppm, from about 300 ppm to about 500 ppm, from about 300 ppm to about 400 ppm, from about 400 ppm to about 800 ppm, or from about 400 ppm to about 500 ppm, based on the total weight of the pre-dried separator. In some embodiments, the water content in the pre-dried separator is less than 500 ppm, less than 400 ppm, less than 300 ppm, less than 200 ppm, less than 100 ppm, or less than 50 ppm by weight, based on the total weight of the pre-dried separator.

In certain embodiments, the dried electrode assembly may have a water content from about 20 ppm to 350 ppm, from about 20 ppm to 300 ppm, from about 20 ppm to 250 ppm, from about 20 ppm to 200 ppm, from about 20 ppm to about 100 ppm, from about 20 ppm to about 50 ppm, from about 50 ppm to about 350 ppm, from about 50 ppm to about 250 ppm, from about 50 ppm to about 150 ppm, from about 100 ppm to about 350 ppm, from about 100 ppm to about 300 ppm, from about 100 ppm to about 250 ppm, from about 100 ppm to about 200 ppm, from about 100 ppm to about 150 ppm, from about 150 ppm to about 350 ppm, from about 150 ppm to about 300 ppm, from about 150 ppm to about 250 ppm, from about 150 ppm to about 200 ppm, from about 200 ppm to about 350 ppm, from about 250 ppm to about 350 ppm, or from about 300 ppm to about 350 ppm, based on the total weight of the dried electrode assembly.

In some embodiments, the dried separator may have a water content from about 50 ppm to about 500 ppm, from about 50 ppm to 400 ppm, from about 50 ppm to about 300 ppm, from about 50 ppm to 200 ppm, from about 50 ppm to 100 ppm, from about 100 ppm to about 500 ppm, from about 100 ppm to about 300 ppm, from about 200 ppm to about 500 ppm, from about 300 ppm to about 500 ppm, or from about 400 ppm to about 500 ppm, based on the total weight of the dried separator.

FIG. 6 shows the discharge curves of three batteries comprising a cathode prepared respectively using an NMP-based slurry, an aqueous slurry containing untreated cathode active material and an aqueous slurry containing base-treated cathode active material in accordance with the present invention. As illustrated in the graph, the battery with the base-treated aqueous slurry of the present invention exhibits better discharging performance than the battery with the conventional untreated aqueous slurry. This result provides further evidence that the base-treated slurry preparation method of the present invention significantly improves the electrochemical performance of the battery. Furthermore, it is evident that the method disclosed in this invention is advantageous over the conventional water-based method.

When compared to the battery with the NMP-based slurry, the battery with the base-treated aqueous slurry of the present invention exhibits a similar discharge performance, as shown in FIG. 6 . However, by using aqueous solvents and water-soluble materials, the method of the present invention reduces the environmental impact of the manufacturing process, as well as lowers production cost as water-soluble materials are generally less expensive and require fewer specialized equipment to handle. Therefore, the present invention can produce lithium-ion batteries more cheaply and in a more environmentally-friendly way without sacrificing battery performance.

The following examples are presented to exemplify embodiments of the invention but are not intended to limit the invention to the specific embodiments set forth. Unless indicated to the contrary, all parts and percentages are by weight. All numerical values are approximate. When numerical ranges are given, it should be understood that embodiments outside the stated ranges may still fall within the scope of the invention. Specific details described in each example should not be construed as necessary features of the invention.

EXAMPLES

The pH value of the slurry was measured by an electrode-type pH meter (ION 2700, Eutech Instruments). The viscosity of slurry was measured using a rotational viscosity meter (NDJ-5S, Shanghai JT Electronic Technology Co. Ltd., China).

The peeling strengths of the dried electrode layers were measured by a tensile testing machine (DZ-106A, obtained from Dongguan Zonhow Test Equipment Co. Ltd., China). This test measures the average force required to peel an electrode layer from the current collector at 1800 angle in Newtons per 18 mm width of the test sample. A strip of adhesion tape (3M; US; model no. 810) with a width of 18 mm was attached onto the surface of the cathode electrode layer. The cathode strip was clipped onto the testing machine and the tape was folded back on itself at 180 degrees, and placed in a moveable jaw and pulled at room temperature and a peel rate of 200 mm per minute. The maximum stripping force measured was taken as the peeling strength. Measurements were repeated three times to find the average value.

The water content in the electrode assembly was measured by Karl-Fischer titration. The electrode assembly was cut into small pieces of 1 cm×1 cm in a glove box filled with argon gas. The cut electrode assembly having a size of 1 cm×1 cm was weighed in a sample vial. The weighed electrode assembly was then added into a titration vessel for Karl Fischer titration using a Karl Fischer coulometry moisture analyzer (831 KF Coulometer, Metrohm, Switzerland). Measurements were repeated three times to find the average value.

The water content in the separator was measured by Karl-Fischer titration. The electrode assembly was cut into small pieces of 1 cm×1 cm in a glove box filled with argon gas. The electrode assembly was separated into the anode, cathode and separator layers. The water contents of the separated separator layers were analyzed by Karl Fischer titration as described above. Measurements were repeated three times to find the average value.

Example 1

A) Preparation of Positive Electrode

1.28 g of ammonia solution (28 wt. %) was diluted with 5.87 g of deionized water to produce an aqueous solution at 25° C. with an ammonia concentration of 5 wt. %. After the addition, the aqueous solution was further stirred for about 5 minutes at 25° C. Thereafter, a first suspension was prepared by dispersing 47 g of NMC532 (obtained from Henan Kelong NewEnergy Co., Ltd., Xinxiang, China) in the aqueous solution at 25° C. The first suspension was sealed and left to rest at 25° C. for 30 minutes.

A second suspension was prepared by dispersing 1.5 g of conductive agent (SuperP; obtained from Timcal Ltd, Bodio, Switzerland) and 10 g of binder (LA138, 85% water content, Chengdu Indigo Power Sources Co., Ltd., China) in 5.79 g of deionized water while stirring with an overhead stirrer (R20, IKA). After the addition, the second suspension was further stirred for about 30 minutes at 25° C. at a speed of 1,200 rpm.

A third suspension with an ammonia concentration of 0.5 wt. % was prepared by adding the first suspension to the second suspension at 25° C. while stirring with an overhead stirrer. Then, the third suspension was degassed under a pressure of about 10 kPa for 1 hour. Then, the third suspension was further stirred for about 60 minutes at 25° C. at a speed of 1,200 rpm to form a homogenized cathode slurry.

The homogenized cathode slurry was coated onto one side of a carbon-coated aluminum foil having a thickness of 14 μm as a current collector using a doctor blade coater with a gap width of 60 μm. The thickness of the carbon coating was 1 μm. The coated slurry film on the aluminum foil was dried to form a cathode electrode layer by an electrically heated conveyor oven (TH-1A, obtained from Nanjing Tonghao Drying Equipment Co. Ltd., China) at 50° C. at a conveyor speed of about 5 meters/minute. The drying time was about 6 minutes. The electrode was then pressed to decrease the thickness of the cathode electrode layer to 35 μm.

B) Preparation of Negative Electrode

A negative electrode slurry was prepared by mixing 90 wt. % of hard carbon (HC; purity of 99.5%, obtained from Ruifute Technology Ltd., Shenzhen, Guangdong, China) with 1.5 wt. % carboxymethyl cellulose (CMC, BSH-12, DKS Co. Ltd., Japan) and 3.5 wt. % SBR (AL-2001, NIPPON A&L INC., Japan) as a binder, and 5 wt. % carbon black as a conductive agent in deionized water. The solid content of the anode slurry was 50 wt. %. The slurry was coated onto one side of a copper foil having a thickness of 8 μm using a doctor blade with a gap width of about 55 μm. The coated film on the copper foil was dried at about 50° C. for 2.4 minutes by a hot air dryer to obtain a negative electrode. The electrode was then pressed to decrease the thickness of the coating to 30 μm and the surface density was 10 mg/cm².

C) Assembling of Coin Cell

CR2032 coin-type Li cells were assembled in an argon-filled glove box. The coated cathode and anode sheets were cut into disc-form positive and negative electrodes, which were then assembled into an electrode assembly by stacking the cathode and anode electrode plates alternatively and then packaged in a case made of an aluminum-plastic laminated film. The cathode and anode electrode plates were kept apart by separators and the case was pre-formed. The separator was a ceramic coated microporous membrane made of nonwoven fabric (MPM, Japan), which had a thickness of about 25 μm. The electrode assembly was then dried in a box-type resistance oven under vacuum (DZF-6020, obtained from Shenzhen Kejing Star Technology Co. Ltd., China) at 105° C. for about 16 hours. The water content of the separator and electrode assembly after drying was 200 ppm and 300 ppm respectively.

An electrolyte was then injected into the case holding the packed electrodes under a high-purity argon atmosphere with a moisture and oxygen content of less than 3 ppm respectively. The electrolyte was a solution of LiPF₆ (1 M) in a mixture of ethylene carbonate (EC), ethyl methyl carbonate (EMC) and dimethyl carbonate (DMC) at a volume ratio of 1:1:1. After electrolyte filling, the coin cell was vacuum sealed and then mechanically pressed using a punch tooling with a standard circular shape.

D) Electrochemical Measurements

The coin cells were analyzed in a constant current mode using a multi-channel battery tester (BTS-4008-5V10 mA, obtained from Neware Electronics Co. Ltd, China). After 1 cycle at C/20 was completed, they were charged and discharged at a rate of C/2. The charging/discharging cycling tests of the cells were performed between 3.0 and 4.3 V at a current density of C/2 at 25° C. to obtain the discharge capacity. The electrochemical performance of the coin cell of Example 1 was measured and is shown in Table 1 below.

Example 2

A positive electrode was prepared in the same manner as in Example 1, except that the aqueous solution was formed by diluting 2.83 g of ammonia solution (28 wt. %) with 13 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 4.99 g of deionized water, so that a third suspension with an ammonia concentration of 1 wt. % was formed when the first suspension was added to the second suspension.

Example 3

A positive electrode was prepared in the same manner as in Example 1, except that the aqueous solution was formed by diluting 4.87 g of ammonia solution (28 wt. %) with 22.4 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 5.14 g of deionized water, so that a third suspension with an ammonia concentration of 1.5 wt. % was formed when the first suspension was added to the second suspension.

Example 4

A positive electrode was prepared in the same manner as in Example 1, except that the aqueous solution had an ammonia concentration of 10 wt. % and was formed by diluting 2.55 g of ammonia solution (28 wt. %) with 4.59 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 5.79 g of deionized water, so that a third suspension with an ammonia concentration of 1 wt. % was formed when the first suspension was added to the second suspension.

Example 5

A positive electrode was prepared in the same manner as in Example 4, except that the aqueous solution was formed by diluting 4.12 g of ammonia solution (28 wt. %) with 7.42 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 6.88 g of deionized water, so that a third suspension with an ammonia concentration of 1.5 wt. % was formed when the first suspension was added to the second suspension.

Example 6

A positive electrode was prepared in the same manner as in Example 1, except that the aqueous solution had an ammonia concentration of 2 wt. % and was formed by diluting 1.49 g of ammonia solution (28 wt. %) with 19.3 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 4 g of deionized water, so that a third suspension with an ammonia concentration of 0.5 wt. % was formed when the first suspension was added to the second suspension.

Example 7

A positive electrode was prepared in the same manner as in Example 1, except that the aqueous solution had a concentration of 15 wt. % and was formed by diluting 2.55 g of ammonia solution (28 wt. %) with 2.21 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 8.17 g of deionized water, so that a third suspension with an ammonia concentration of 1 wt. % was formed when the first suspension was added to the second suspension.

Example 8

A positive electrode was prepared in the same manner as in Example 7, except that the aqueous solution was formed by diluting 3.83 g of ammonia solution (28 wt. %) with 3.32 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 5.79 g of deionized water, so that a third suspension with an ammonia concentration of 1.5 wt. % was formed when the first suspension was added to the second suspension.

Example 9

A positive electrode was prepared in the same manner as in Example 1, except that the aqueous solution was a 10 wt. % dimethylamine solution that was formed by diluting 0.71 g of dimethylamine solution (anhydrous; ≥99% purity) with 6.43 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 5.79 g of deionized water, so that a third suspension with a dimethylamine concentration of 1 wt. % was formed when the first suspension was added to the second suspension.

Example 10

A positive electrode was prepared in the same manner as in Example 1, except that the aqueous solution was a 10 wt. % trimethylamine solution that was formed by diluting 0.71 g of trimethylamine solution (anhydrous; ≥99% purity) with 6.43 g of deionized water, and the second suspension was prepared by mixing 10 g of LA133 binder (85% water content; obtained from Chengdu Indigo Power Sources Co., Ltd., China) and 1.5 g of conductive agent (SuperP; obtained from Timcal Ltd, Bodio, Switzerland) in 5.79 g of deionized water, so that a third suspension with a trimethylamine concentration of 1 wt. % was formed when the first suspension was added to the second suspension.

Example 11

A positive electrode was prepared in the same manner as in Example 10, except that the aqueous solution was formed by diluting 1.15 g of trimethylamine solution (anhydrous; ≥99% purity) with 10.4 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 6.88 g of deionized water, so that a third suspension with a trimethylamine concentration of 1.5 wt. % was formed when the first suspension was added to the second suspension.

Example 12

A positive electrode was prepared in the same manner as in Example 10, except that the aqueous solution was formed by diluting 1.59 g of trimethylamine solution (anhydrous; 299% purity) with 14.3 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 4.99 g of deionized water, so that a third suspension with a trimethylamine concentration of 2 wt. % was formed when the first suspension was added to the second suspension.

Example 13

A positive electrode was prepared in the same manner as in Example 4, except that the 10 g of LA138 binder was replaced with polyacrylonitrile (PAN) (85% water content) of the same weight.

Example 14

A positive electrode was prepared in the same manner as in Example 4, except that the second suspension was prepared by mixing 1.5 g of conductive agent and a 3 g mixture (50% water content) of styrene-butadiene rubber (SBR) and carboxymethyl cellulose (CMC) in 12.8 g of deionized water, wherein the weight ratio of SBR to CMC was 3 to 1.

Example 15

A positive electrode was prepared in the same manner as in Example 4, except that the second suspension was prepared by mixing 1.5 g of conductive agent and 15 g of sodium alginate (10 wt. % solution) in 0.79 g of deionized water.

Example 16

A positive electrode was prepared in the same manner as in Example 4, except that the second suspension was prepared by mixing 1.5 g of conductive agent and 3.33 g of latex (55% water content) in 14.3 g of deionized water.

Example 17

A positive electrode was prepared in the same manner as in Example 4, except the homogenized cathode slurry was coated on an aluminum foil with no carbon coating.

Comparative Example 1

A positive electrode slurry was prepared by dispersing 47 g of NMC532 (obtained from Henan Kelong NewEnergy Co., Ltd., Xinxiang, China), 1.5 g of conductive agent (SuperP; obtained from Timcal Ltd, Bodio, Switzerland) and 10 g of LA138 binder (85% water content, Chengdu Indigo Power Sources Co., Ltd., China) in 5.79 g of deionized water while stirring with an overhead stirrer. The slurry was degassed under a pressure of about 10 kPa for 1 hour. Then, the slurry was further stirred for about 60 minutes at 25° C. at a speed of 1,200 rpm.

The homogenized cathode slurry was coated onto one side of an aluminum foil having a thickness of 13 μm as a current collector using a doctor blade coater with a gap width of 45 μm. The coated slurry film on the aluminum foil was dried to form a cathode electrode layer by an electrically heated conveyor oven (TH-1A, obtained from Nanjing Tonghao Drying Equipment Co. Ltd., China) at 50° C. at a conveyor speed of about 5 meters/minute. The drying time was about 6 minutes. The electrode was then pressed to decrease the thickness of the cathode electrode layer to 35 μm.

Comparative Example 2

A positive electrode slurry was prepared by dispersing 47 g of NMC532 (obtained from Henan Kelong NewEnergy Co., Ltd., Xinxiang, China), 1.5 g of conductive agent (SuperP; obtained from Timcal Ltd, Bodio, Switzerland) and 15 g of polyvinylidene fluoride binder (PVDF; 10 wt. % solution in NMP; Solef® 5130, obtained from Solvay S.A., Belgium) in 7.93 g of N-methyl-2-pyrrolidone (NMP; ≥99%, Sigma-Aldrich, USA) while stirring with an overhead stirrer. The slurry was degassed under a pressure of about 10 kPa for 1 hour. Then, the slurry was further stirred for about 60 minutes at 25° C. at a speed of 1,200 rpm.

The homogenized cathode slurry was coated onto one side of an aluminum foil having a thickness of 13 μm as a current collector using a doctor blade coater with a gap width of 45 μm. The coated slurry film on the aluminum foil was dried to form a cathode electrode layer by an electrically heated conveyor oven (TH-1A, obtained from Nanjing Tonghao Drying Equipment Co. Ltd., China) at 50° C. at a conveyor speed of about 5 meters/minute. The drying time was about 6 minutes. The electrode was then pressed to decrease the thickness of the cathode electrode layer to 35 μm.

Comparative Example 3

A positive electrode was prepared in the same manner as in Example 17, except that the aqueous solution was a 10 wt. % citric acid solution that was prepared by adding 0.71 g of citric acid into 6.43 g of deionized water.

Preparation of Negative Electrode of Examples 2-17 and Comparative Examples 1-3

The negative electrodes of Examples 2-17 and Comparative Examples 1-3 were prepared in the same manner as in Example 1.

Assembling of Coin Cells of Examples 2-17 and Comparative Examples 1-3

The coin cells of Examples 2-17 and Comparative Examples 1-3 were assembled in the same manner as in Example 1.

Electrochemical Measurements of Examples 2-17 and Comparative Examples 1-3

The electrochemical performance of the coin cells of Examples 2-17 and Comparative Examples 1-3 was measured in the same manner as in Example 1 and the test results are shown in Table 1 below.

Example 18

A positive electrode was prepared in the same manner as in Example 1, except that the 47 g of NMC532 was replaced with NMC622 (obtained from Henan Kelong NewEnergy Co., Ltd., Xinxiang, China) of the same weight.

Example 19

A positive electrode was prepared in the same manner as in Example 18, except that the aqueous solution was formed by diluting 2.83 g of ammonia solution (28 wt. %) with 13 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 4.99 g of deionized water, so that a third suspension with an ammonia concentration of 1 wt. % was formed when the first suspension was added to the second suspension.

Example 20

A positive electrode was prepared in the same manner as in Example 18, except that the aqueous solution was formed by diluting 4.87 g of ammonia solution (28 wt. %) with 22.4 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 5.14 g of deionized water, so that a third suspension with an ammonia concentration of 1.5 wt. % was formed when the first suspension was added to the second suspension.

Example 21

A positive electrode was prepared in the same manner as in Example 18, except that the aqueous solution was formed by diluting 7.44 g of ammonia solution (28 wt. %) with 34.2 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 4 g of deionized water, so that a third suspension with an ammonia concentration of 2 wt. % was formed when the first suspension was added to the second suspension.

Example 22

A positive electrode was prepared in the same manner as in Example 18, except that the aqueous solution had an ammonia concentration of 7 wt. % and was formed by diluting 4.25 g of ammonia solution (28 wt. %) with 12.8 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 3.86 g of deionized water, so that a third suspension with an ammonia concentration of 1.5 wt. % was formed when the first suspension was added to the second suspension.

Example 23

A positive electrode was prepared in the same manner as in Example 18, except that the aqueous solution had an ammonia concentration of 10 wt. % and was formed by diluting 2.55 g of ammonia solution (28 wt. %) with 4.59 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 5.79 g of deionized water, so that a third suspension with an ammonia concentration of 1 wt. % was formed when the first suspension was added to the second suspension.

Example 24

A positive electrode was prepared in the same manner as in Example 23, except that the aqueous solution was formed by diluting 4.12 g of ammonia solution (28 wt. %) with 7.42 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 6.88 g of deionized water, so that a third suspension with an ammonia concentration of 1.5 wt. % was formed when the first suspension was added to the second suspension.

Example 25

A positive electrode was prepared in the same manner as in Example 23, except that the aqueous solution was formed by diluting 5.67 g of ammonia solution (28 wt. %) with 10.2 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 4.99 g of deionized water, so that a third suspension with an ammonia concentration of 2 wt. % was formed when the first suspension was added to the second suspension.

Example 26

A positive electrode was prepared in the same manner as in Example 18, except that the aqueous solution had an ammonia concentration of 13 wt. % and was formed by diluting 3.83 g of ammonia solution (28 wt. %) with 4.42 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 4.69 g of deionized water, so that a third suspension with an ammonia concentration of 1.5 wt. % was formed when the first suspension was added to the second suspension.

Example 27

A positive electrode was prepared in the same manner as in Example 18, except that the aqueous solution had an ammonia concentration of 15 wt. % and was formed by diluting 2.38 g of ammonia solution (28 wt. %) with 2.06 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 3.72 of deionized water, so that a third suspension with an ammonia concentration of 1 wt. % was formed when the first suspension was added to the second suspension.

Example 28

A positive electrode was prepared in the same manner as in Example 27, except that the aqueous solution was formed by diluting 3.83 g of ammonia solution (28 wt. %) with 3.32 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 5.79 g of deionized water, so that a third suspension with an ammonia concentration of 1.5 wt. % was formed when the first suspension was added to the second suspension.

Example 29

A positive electrode was prepared in the same manner as in Example 27, except that the aqueous solution was formed by diluting 5.1 g of ammonia solution (28 wt. %) with 4.42 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 3.4 g of deionized water, so that a third suspension with an ammonia concentration of 2 wt. % was formed when the first suspension was added to the second suspension.

Example 30

A positive electrode was prepared in the same manner as in Example 24, except that the homogenized cathode slurry was coated on an aluminum foil without a carbon coating.

Comparative Example 4

A positive electrode slurry was prepared by dispersing 47 g of NMC622 (obtained from Henan Kelong NewEnergy Co., Ltd., Xinxiang, China), 1.5 g of conductive agent (SuperP; obtained from Timcal Ltd, Bodio, Switzerland) and 10 g of LA138 binder (85% water content; obtained from Chengdu Indigo Power Sources Co., Ltd.) in 18.4 g of deionized water while stirring with an overhead stirrer. The slurry was degassed under a pressure of about 10 kPa for 1 hour. Then, the slurry was further stirred for about 60 minutes at 25° C. at a speed of 1,200 rpm.

The homogenized cathode slurry was coated onto one side of an aluminum foil having a thickness of 13 μm as a current collector using a doctor blade coater with a gap width of 45 μm. The coated slurry film on the aluminum foil was dried to form a cathode electrode layer by an electrically heated conveyor oven (TH-1A, obtained from Nanjing Tonghao Drying Equipment Co. Ltd., China) at 50° C. at a conveyor speed of about 5 meters/minute. The drying time was about 6 minutes. The electrode was then pressed to decrease the thickness of the cathode electrode layer to 35 μm.

Comparative Example 5

A positive electrode was prepared in the same manner as in Comparative Example 4, except that the homogenized cathode slurry was coated onto an aluminum foil with a carbon coating having a thickness of 1 μm.

Comparative Example 6

A positive electrode slurry was prepared by dispersing 47 g of NMC622 (obtained from Henan Kelong NewEnergy Co., Ltd., Xinxiang, China), 1.5 g of conductive agent (SuperP; obtained from Timcal Ltd, Bodio, Switzerland) and 15 g of PVDF binder (10 wt. % solution in NMP; Solef® 5130, obtained from Solvay S.A., Belgium) in 13.4 g of NMP (≥99%, Sigma-Aldrich, USA) while stirring with an overhead stirrer. The slurry was degassed under a pressure of about 10 kPa for 1 hour. Then, the slurry was further stirred for about 60 minutes at 25° C. at a speed of 1,200 rpm.

The homogenized cathode slurry was coated onto one side of an aluminum foil having a thickness of 13 μm as a current collector using a doctor blade coater with a gap width of 45 μm. The coated slurry film on the aluminum foil was dried to form a cathode electrode layer by an electrically heated conveyor oven (TH-1A, obtained from Nanjing Tonghao Drying Equipment Co. Ltd., China) at 50° C. at a conveyor speed of about 5 meters/minute. The drying time was about 6 minutes. The electrode was then pressed to decrease the thickness of the cathode electrode layer to 35 μm.

Comparative Example 7

4.12 g of ammonia solution (28 wt. %) was diluted with 7.42 g deionized water to produce an aqueous solution at 25° C. with an ammonia concentration of 10 wt. %. After the addition, the aqueous solution was further stirred for about 5 minutes at 25° C. Thereafter, a first suspension was prepared by dispersing 47 g of NMC622 (obtained from Henan Kelong NewEnergy Co., Ltd., Xinxiang, China) in the aqueous solution at 25° C. The first suspension was sealed and left to rest at 25° C. for 30 minutes. The cathode material was then filtered and dried in a box-type resistance oven under vacuum (DZF-6020, obtained from Shenzhen Kejing Star Technology Co. Ltd., China) at 60° C. The drying time was about 12 hours.

A positive electrode slurry was prepared by dispersing all of the dried cathode material, 1.5 g of conductive agent (SuperP; obtained from Timcal Ltd, Bodio, Switzerland) and 10 g of binder (LA138; 85% water content, Chengdu Indigo Power Sources Co., Ltd., China) in 26.9 g of deionized water (≥99%, Sigma-Aldrich, USA) while stirring with an overhead stirrer. The slurry was degassed under a pressure of about 10 kPa for 1 hour. Then, the slurry was further stirred for about 60 minutes at 25° C. at a speed of 1,200 rpm.

The homogenized cathode slurry was coated onto one side of an aluminum foil having a thickness of 13 μm as a current collector using a doctor blade coater (MSK-AFA-III, obtained from Shenzhen Kejing Star Technology Ltd., China) with a gap width of 45 μm. The coated film on the aluminum foil was dried in a box-type resistance oven (DZF-6020, obtained from Shenzhen Kejing Star Technology Co. Ltd., China) at 50° C. The drying time was about 6 minutes. The electrode was then pressed to decrease the thickness of the cathode electrode layer to 35 μm.

Comparative Example 8

A positive electrode was prepared in the same manner as in Comparative Example 7, except that the 10 g of LA138 binder was replaced with 15 g of PVDF (Solef® 5130, obtained from Solvay S.A., Belgium), and the 26.9 g of deionized water to form the slurry was replaced with 21.9 g of NMP (≥99%, Sigma-Aldrich, USA).

Preparation of Negative Electrode of Examples 18-30 and Comparative Examples 4-8

The negative electrodes of Examples 18-30 and Comparative Examples 4-8 were prepared in the same manner as in Example 1.

Assembling of Coin Cell of Examples 18-30 and Comparative Examples 4-8

The coin cells of Examples 18-30 and Comparative Examples 4-8 were assembled in the same manner as in Example 1.

Electrochemical Measurements of Examples 18-30 and Comparative Examples 4-8

The electrochemical performance of the coin cells of Examples 18-30 and Comparative Examples 4-8 was measured in the same manner as in Example 1 and the test results are shown in Table 2 below.

Example 31

A positive electrode was prepared in the same manner as in Example 19, except that the 47 g of NMC622 was replaced with NMC811 of the same weight, and the 10 g of LA138 binder was replaced with LA133 of the same weight.

Example 32

A positive electrode was prepared in the same manner as in Example 31, except that the aqueous solution was formed by diluting 4.87 g of ammonia solution (28 wt. %) with 22.4 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 5.14 g of deionized water, so that a third suspension with an ammonia concentration of 1.5 wt. % was formed when the first suspension was added to the second suspension.

Example 33

A positive electrode was prepared in the same manner as in Example 31, except that the aqueous solution was formed by diluting 7.6 g of ammonia solution (28 wt. %) with 35 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 5.33 g of deionized water, so that a third suspension with an ammonia concentration of 2 wt. % was formed when the first suspension was added to the second suspension.

Example 34

A positive electrode was prepared in the same manner as in Example 31, except that the aqueous solution had an ammonia concentration of 10 wt. % and was formed by diluting 4 g of ammonia solution (28 wt. %) with 7.2 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 4.93 g of deionized water, so that a third suspension with an ammonia concentration of 1.5 wt. % was formed when the first suspension was added to the second suspension.

Example 35

A positive electrode was prepared in the same manner as in Example 34, except that the aqueous solution was formed by diluting 5.67 g of ammonia solution (28 wt. %) with 10.2 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 4.99 g of deionized water, so that a third suspension with an ammonia concentration of 2 wt. % was formed when the first suspension was added to the second suspension.

Example 36

A positive electrode was prepared in the same manner as in Example 34, except that the aqueous solution was formed by diluting 7.44 g of ammonia solution (28 wt. %) with 13.4 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 4 g of deionized water, so that a third suspension with an ammonia concentration of 2.5 wt. % was formed when the first suspension was added to the second suspension.

Example 37

A positive electrode was prepared in the same manner as in Example 34, except that the aqueous solution was formed by diluting 12 g of ammonia solution (28 wt. %) with 21.6 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 4 g of deionized water, so that a third suspension with an ammonia concentration of 3.5 wt. % was formed when the first suspension was added to the second suspension.

Example 38

A positive electrode was prepared in the same manner as in Example 31, except that the aqueous solution had an ammonia concentration of 15 wt. % and was formed by diluting 3.83 g of ammonia solution (28 wt. %) with 3.32 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 5.79 g of deionized water, so that a third suspension with an ammonia concentration of 1.5 wt. % was formed when the first suspension was added to the second suspension.

Example 39

A positive electrode was prepared in the same manner as in Example 38, except that the aqueous solution was formed by diluting 5.1 g of ammonia solution (28 wt. %) with 4.42 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 3.4 g of deionized water, so that a third suspension with an ammonia concentration of 2 wt. % was formed when the first suspension was added to the second suspension.

Example 40

A positive electrode was prepared in the same manner as in Example 38, except that the aqueous solution was formed by diluting 6.66 g of ammonia solution (28 wt. %) with 5.77 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 3.69 g of deionized water, so that a third suspension with an ammonia concentration of 2.5 wt. % was formed when the first suspension was added to the second suspension.

Example 41

A positive electrode was prepared in the same manner as in Example 38, except that the aqueous solution was formed by diluting 8.5 g of ammonia solution (28 wt. %) with 7.37 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 4.99 g of deionized water, so that a third suspension with an ammonia concentration of 3 wt. % was formed when the first suspension was added to the second suspension.

Example 42

A positive electrode was prepared in the same manner as in Example 38, except that the aqueous solution was formed by diluting 10.4 g of ammonia solution (28 wt. %) with 9.03 g of deionized water, and the second suspension was prepared by mixing the binder and conductive agent in 5.39 g of deionized water, so that a third suspension with an ammonia concentration of 3.5 wt. % was formed when the first suspension was added to the second suspension.

Example 43

A positive electrode was prepared in the same manner as in Example 35, except that the first suspension was sealed and left to rest for 10 minutes.

Example 44

A positive electrode was prepared in the same manner as in Example 35, except that the first suspension was sealed and left to rest for 60 minutes.

Example 45

A positive electrode was prepared in the same manner as in Example 35, except that the first suspension was not sealed and left to rest, but actively stirred at 25° C. for 10 minutes with an overhead stirrer at a speed of 1,200 rpm.

Example 46

A positive electrode slurry was prepared in the same manner as in Example 35, except that the first suspension was not sealed and left to rest, but actively stirred at 25° C. for 60 minutes with an overhead stirrer at a speed of 1,200 rpm.

Example 47

A positive electrode slurry was prepared in the same manner as in Example 35, except that the homogenized cathode slurry was coated on an aluminum foil without a carbon coating.

Example 48

A positive electrode was prepared in the same manner as in Example 35, except that the 47 g of NMC811 was replaced with NCA of the same weight.

Example 49

A positive electrode was prepared in the same manner as in Example 4, except that the 47 g of NMC532 was replaced with a core-shell cathode active material (C-S) comprising NMC532 as the core and Li_(0.95)Ni_(0.53)Mn_(0.29)Co_(0.15)Al_(0.03)O₂ as the shell. The cathode active material has a particle size D50 of about 35 μm. The thickness of the shell was about 3 μm.

Example 50

A positive electrode was prepared in the same manner as in Example 4, except that the 47 g of NMC532 was replaced with a core-shell cathode active material (C-S) comprising NMC622 as the core and Li_(0.95)Ni_(0.53)Mn_(0.29)Co_(0.15)Al_(0.03)O₂ as the shell. The cathode active material has a particle size D50 of about 35 μm. The thickness of the shell was about 3 μm.

Comparative Example 9

A positive electrode slurry was prepared by dispersing 47 g of NMC811 (obtained from Henan Kelong NewEnergy Co., Ltd., Xinxiang, China), 1.5 g of conductive agent (SuperP; obtained from Timcal Ltd, Bodio, Switzerland) and 10 g of LA133 binder (85% water content; obtained from Chengdu Indigo Power Sources Co., Ltd.) in 20.9 g of deionized water while stirring with an overhead stirrer. The slurry was degassed under a pressure of about 10 kPa for 1 hour. Then, the slurry was further stirred for about 60 minutes at 25° C. at a speed of 1,200 rpm.

The homogenized cathode slurry was coated onto one side of an aluminum foil having a thickness of 13 μm as a current collector using a doctor blade coater with a gap width of 45 μm. The coated slurry film on the aluminum foil was dried to form a cathode electrode layer by an electrically heated conveyor oven (TH-1A, obtained from Nanjing Tonghao Drying Equipment Co. Ltd., China) at 50° C. at a conveyor speed of about 5 meters/minute. The drying time was about 6 minutes. The electrode was then pressed to decrease the thickness of the cathode electrode layer to 35 μm.

Comparative Example 10

A positive electrode slurry was prepared in the same manner as in Comparative Example 9, except that the homogenized cathode slurry was coated on an aluminum foil with a carbon coating having a thickness of 1 μm.

Comparative Example 11

A positive electrode slurry was prepared by dispersing 47 g of NMC811 (obtained from Henan Kelong NewEnergy Co., Ltd., Xinxiang, China), 1.5 g of conductive agent (SuperP; obtained from Timcal Ltd, Bodio, Switzerland) and 15 g of PVDF (Solef® 5130, obtained from Solvay S.A., Belgium) in 15.9 g of NMP (≥99%, Sigma-Aldrich, USA) while stirring with an overhead stirrer. The slurry was degassed under a pressure of about 10 kPa for 1 hour. Then, the slurry was further stirred for about 60 minutes at 25° C. at a speed of 1,200 rpm.

The homogenized cathode slurry was coated onto one side of an aluminum foil having a thickness of 13 μm as a current collector using a doctor blade coater with a gap width of 45 μm. The coated slurry film on the aluminum foil was dried to form a cathode electrode layer by an electrically heated conveyor oven (TH-1A, obtained from Nanjing Tonghao Drying Equipment Co. Ltd., China) at 50° C. at a conveyor speed of about 5 meters/minute. The drying time was about 6 minutes. The electrode was then pressed to decrease the thickness of the cathode electrode layer to 35 μm.

Preparation of Negative Electrode of Examples 31-50 and Comparative Examples 9-11

The negative electrodes of Examples 31-50 and Comparative Examples 9-11 were prepared in the same manner as in Example 1.

Assembling of Coin Cell of Examples 31-50 and Comparative Examples 9-11

The coin cells of Examples 31-50 and Comparative Examples 9-11 were assembled in the same manner as in Example 1.

Electrochemical Measurements of Examples 31-50 and Comparative Examples 9-11

The electrochemical performance of the coin cells of Examples 31-50 and Comparative Examples 9-11 was measured in the same manner as in Example 1 and the test results are shown in Table 3 below.

TABLE 1 Homogenization of 0.5 C Capacity Aqueous solution Treatment in third suspension Initial retention Cathode Base first suspension Base pH of discharging after active conc. Temp Time conc. Temp Time cathode slurry capacity 50 cycles material Base (%) pH (° C.) (mins) Solvent (%) (° C.) (hrs) Beginning End (mAh/g) (%) Example 1 NMC532 NH₃ 5 12.0 25 30 Water 0.5 25 1 11.8 11.5 145 83.7 Example 2 NMC532 NH₃ 5 11.9 25 30 Water 1 25 1 11.8 11.6 144 83.5 Example 3 NMC532 NH₃ 5 12.0 25 30 Water 1.5 25 1 11.9 11.7 147 82.8 Example 4 NMC532 NH₃ 10 12.1 25 30 Water 1 25 1 12.0 11.7 157 87.9 Example 5 NMC532 NH₃ 10 12.1 25 30 Water 1.5 25 1 12.0 11.7 152 82.6 Example 6 NMC532 NH₃ 2 11.8 25 30 Water 0.5 25 1 11.7 11.5 125 80.3 Example 7 NMC532 NH₃ 15 12.3 25 30 Water 1 25 1 12.1 11.9 147 85.1 Example 8 NMC532 NH₃ 15 12.3 25 30 Water 1.5 25 1 12.2 11.9 149 82.5 Example 9 NMC532 NH(CH₃)₂ 10 12.1 25 30 Water 1 25 1 11.9 11.6 147 83.8 Example 10 NMC532 N(CH₃)₃ 10 12.0 25 30 Water 1 25 1 11.9 11.6 142 85.8 Example 11 NMC532 N(CH₃)₃ 10 12.1 25 30 Water 1.5 25 1 12.0 11.7 145 83.5 Example 12 NMC532 N(CH₃)₃ 10 12.0 25 30 Water 2 25 1 11.9 11.6 134 83.6 Example 13 NMC532 NH₃ 10 12.1 25 30 Water 1 25 1 12.0 11.7 152 84.2 Example 14 NMC532 NH₃ 10 12.1 25 30 Water 1 25 1 11.9 11.7 148 83.1 Example 15 NMC532 NH₃ 10 12.0 25 30 Water 1 25 1 11.9 11.6 149 82.7 Example 16 NMC532 NH₃ 10 12.1 25 30 Water 1 25 1 11.9 11.6 150 83.7 Example 17 NMC532 NH₃ 10 12.1 25 30 Water 1 25 1 12.0 11.7 152 84.3 Comparative NMC532 — — — — — Water — 25 1 11.7 11.5 124 80.2 Example 1 Comparative NMC532 — — — — — NMP — 25 1 11.7 11.8 158 84.2 Example 2 Comparative NMC532 Citric 10 11.0 25 30 Water 1 25 1 10.9 11.1 111 75.3 Example 3 acid* *Treated in acid for comparison against treatment in base

TABLE 2 Homogenization of 0.5 C Capacity Aqueous solution Treatment in third suspension Initial retention Cathode Base first suspension Base pH of discharging after active conc. Temp Time conc. Temp Time cathode slurry capacity 50 cycles material Base (%) pH (° C.) (mins) Solvent (%) (° C.) (hrs) Beginning End (mAh/g) (%) Example 18 NMC622 NH₃ 5 12.6 25 30 Water 0.5 25 1 12.5 12.2 153 82.3 Example 19 NMC622 NH₃ 5 12.5 25 30 Water 1 25 1 12.6 12.3 154 82.7 Example 20 NMC622 NH₃ 5 12.6 25 30 Water 1.5 25 1 12.6 12.3 155 83.2 Example 21 NMC622 NH₃ 5 12.6 25 30 Water 2 25 1 12.7 12.4 156 84.1 Example 22 NMC622 NH₃ 7 12.7 25 30 Water 1.5 25 1 12.7 12.3 155 87.3 Example 23 NMC622 NH₃ 10 12.8 25 30 Water 1 25 1 12.6 12.1 155 88.4 Example 24 NMC622 NH₃ 10 12.7 25 30 Water 1.5 25 1 12.7 12.2 160 95.0 Example 25 NMC622 NH₃ 10 12.8 25 30 Water 2 25 1 12.7 12.3 154 85.0 Example 26 NMC622 NH₃ 13 12.9 25 30 Water 1.5 25 1 12.7 12.4 155 86.2 Example 27 NMC622 NH₃ 15 12.9 25 30 Water 1 25 1 12.6 12.3 153 83.7 Example 28 NMC622 NH₃ 15 13.0 25 30 Water 1.5 25 1 12.7 12.3 155 84.5 Example 29 NMC622 NH₃ 15 13.0 25 30 Water 2 25 1 12.8 12.5 152 83.8 Example 30 NMC622 NH₃ 10 12.8 25 30 Water 1.5 25 1 12.7 12.2 150 84.7 Comparative NMC622 — — — — — Water — 25 1 12.2 12.2 145 78.8 Example 4 Comparative NMC622 — — — — — Water — 25 1 12.1 12.2 154 80.2 Example 5 Comparative NMC622 — — — — — NMP — 25 1 12.2 12.5 162 87.3 Example 6 Comparative NMC622 NH₃ 10 12.8 25 30 Water — 25 1 12.2 12.5 147 80.3 Example 7* Comparative NMC622 NH₃ 10 12.7 25 30 NMP — 25 1 12.3 12.2 127 74.2 Example 8* *Cathode active material is thoroughly dried after treatment in base before adding to third suspension

TABLE 3 Homogenization of 0.5 C Capacity Aqueous solution Treatment in third suspension Initial retention Cathode Base first suspension Base pH of discharging after active conc. Temp Time conc. Temp Time cathode slurry capacity 50 cycles material Base (%) pH (° C.) (mins) Solvent (%) (° C.) (hrs) Beginning End (mAh/g) (%) Example 31 NMC811 NH₃ 5 13.2 25 30 Water 1 25 1 13.1 12.7 172 83.2 Example 32 NMC811 NH₃ 5 13.2 25 30 Water 1.5 25 1 13.1 12.8 173 83.7 Example 33 NMC811 NH₃ 5 13.2 25 30 Water 2 25 1 13.2 12.7 175 84.2 Example 34 NMC811 NH₃ 10 13.3 25 30 Water 1.5 25 1 13.1 12.8 186 88 Example 35 NMC811 NH₃ 10 13.2 25 30 Water 2 25 1 13.2 12.9 180 95.7 Example 36 NMC811 NH₃ 10 13.3 25 30 Water 2.5 25 1 13.2 12.8 179 88.8 Example 37 NMC811 NH₃ 10 13.3 25 30 Water 3.5 25 1 13.3 12.9 176 85.9 Example 38 NMC811 NH₃ 15 13.5 25 30 Water 1.5 25 1 13.2 12.9 178 84.8 Example 39 NMC811 NH₃ 15 13.5 25 30 Water 2 25 1 13.3 12.9 177 83.9 Example 40 NMC811 NH₃ 15 13.6 25 30 Water 2.5 25 1 13.4 12.9 176 85.1 Example 41 NMC811 NH₃ 15 13.7 25 30 Water 3 25 1 13.5 13.0 173 85.3 Example 42 NMC811 NH₃ 15 13.6 25 30 Water 3.5 25 1 13.5 13.0 175 85.7 Example 43 NMC811 NH₃ 10 13.2 25 10 Water 2 25 1 13.2 12.9 178 93.6 Example 44 NMC811 NH₃ 10 13.3 25 60 Water 2 25 1 13.3 12.9 179 94.4 Example 45 NMC811 NH₃ 10 13.2 25 10 Water 2 25 1 13.3 12.8 183 88.0 Example 46 NMC811 NH₃ 10 13.3 25 60 Water 2 25 1 13.2 12.9 181 87.3 Example 47 NMC811 NH₃ 10 13.3 25 30 Water 2 25 1 13.2 12.9 163 80.2 Example 48 NCA NH₃ 10 13.1 25 30 Water 2 25 1 13.0 12.8 178 93.3 Example 49 C-S NH₃ 10 12.2 25 30 Water 1 25 1 12.0 11.7 153 86.9 Example 50 C-S NH₃ 10 12.3 25 30 Water 1 25 1 12.1 11.7 155 87.8 Comparative NMC811 — — — — — Water — 25 1 13.2 13.3 169 77.3 Example 9 Comparative NMC811 — — — — — Water — 25 1 13.0 13.2 165 75.2 Example 10 Comparative NMC811 — — — — — NMP — 25 1 13.2 13.7 182 85.7 Example 11

TABLE 4 Undiluted amount Conc. of of Li dissolved % of Li dissolved from ammonia from cathode cathode material relative solution (M) material (ppm)* to pure water treatment 0 35205.768 100.00 2.552 34404.465 97.72 3.318 32258.222 91.63 3.828 31817.213 90.38 4.338 31160.625 88.51 5.104 30619.663 86.97 *Based on total weight of lithium in the cathode material added

While the invention has been described with respect to a limited number of embodiments, the specific features of one embodiment should not be attributed to other embodiments of the invention. In some embodiments, the methods may include numerous steps not mentioned herein. In other embodiments, the methods do not include, or are substantially free of, any steps not enumerated herein. Variations and modifications from the described embodiments exist. The appended claims intend to cover all those modifications and variations as falling within the scope of the invention. 

What is claimed is:
 1. A cathode slurry for a secondary battery, comprising a cathode active material, a binder, a solvent and a base having a formula of R¹R²R³N, wherein each of R¹, R² and R³ is independently H, C₁₋₆ alkyl, C₃₋₆ cycloalkyl, C₁₋₆ heteroalkyl, C₄₋₆ cycloalkylalkyl, C₂₋₆ alkoxyalkyl, or C₃₋₆ alkoxyalkoxyalkyl, where the C₁₋₆ alkyl, C₃₋₆ cycloalkyl, C₁₋₆ heteroalkyl, C₄₋₆ cycloalkylalkyl, C₂₋₆ alkoxyalkyl, or C₃₋₆ alkoxyalkoxyalkyl is optionally substituted with one or more substituents, where each of the substituents is independently alkyl or cycloalkyl, wherein the base is selected from the group consisting of ammonia, methylamine, ethylamine, propylamine, isopropylamine, cyclopropylamine, butylamine, N-butylamine, tert-butylamine, isobutylamine, sec-butylamine, cyclobutylamine, dimethylamine, N-ethylmethylamine, diethylamine, N-methylpropylamine, N-methylcyclopropanamine, N-ethyl-N-propylamine, N,2-dimethyl-1-propanamine, N-tert-butylmethylamine, diisopropylamine, N-methyl-tert-butylamine, trimethylamine, N,N-dimethylethylamine, N,N-diethylmethylamine, N,N-dimethylisopropylamine, triethylamine and combinations thereof, and wherein the cathode slurry has a pH of greater than 8 and less than
 14. 2. The cathode slurry of claim 1, wherein each of R¹, R² and R³ is independently C₁₋₄ alkyl, C₃₋₅ cycloalkyl, C₁₋₄ heteroalkyl, C₂₋₄ alkoxyalkyl, or C₃₋₅ alkoxyalkoxyalkyl.
 3. The cathode slurry of claim 1, wherein each of R¹, R² and R³ is independently H, methyl, ethyl, propyl, isopropyl, cyclopropyl, n-butyl, tert-butyl, isobutyl, sec-butyl, cyclobutyl, pentyl, methoxymethyl, ethoxymethyl, or methoxyethoxymethyl.
 4. The cathode slurry of claim 1, wherein the cathode active material is selected from the group consisting of Li_(1+x)Ni_(a)Mn_(b)Co_(c)Al_((1−a−b−c))O₂, LiNi_(0.33)Mn_(0.33)Co_(0.33)O₂, LiNi_(0.4)Mn_(0.4)Co_(0.2)O₂, LiNi_(0.5)Mn_(0.3)Co_(0.2)O₂, LiNi_(0.6)Mn_(0.2)Co_(0.2)O₂, LiNi_(0.7)Mn_(0.15)Co_(0.15)O₂, LiNi_(0.8)Mn_(0.1)Co_(0.1)O₂, LiNi_(0.92)Mn_(0.04)Co_(0.04)O₂, LiNi_(0.8)Co_(0.15)Al_(0.05)O₂, LiCoO₂, LiNiO₂, LiMnO₂, LiMn₂O₄, Li₂MnO₃, and combinations thereof; wherein −0.2≤x≤0.2, 0≤a<1, 0≤b<1, 0≤c<1, and a+b+c≤1.
 5. The cathode slurry of claim 1, wherein the cathode active material comprises or is a core-shell composite having a core and shell structure, wherein the core and the shell each independently comprise a lithium transition metal oxide selected from the group consisting of Li_(1+x)Ni_(a)Mn_(b)Co_(c)Al_((1−a−b−c))O₂, LiCoO₂, LiNiO₂, LiMnO₂, LiMn₂O₄, Li₂MnO₃, LiCrO₂, Li₄Ti₅O₁₂, LiV₂O₅, LiTiS₂, LiMoS₂, and combinations thereof; wherein −0.2≤x≤0.2, 0≤a<1, 0≤b<1, 0≤c<1, and a+b+c≤1.
 6. The cathode slurry of claim 5, wherein the shell comprises a lithium transition metal oxide selected from the group consisting of LiNi_(0.33)Mn_(0.33)Co_(0.33)O₂, LiNi_(0.4)Mn_(0.4)Co_(0.2)O₂, LiNi_(0.5)Mn_(0.3)Co_(0.2)O₂, LiNi_(0.6)Mn_(0.2)Co_(0.2)O₂, LiNi_(0.7)Mn_(0.15)Co_(0.15)O₂, LiNi_(0.8)Mn_(0.1)Co_(0.1)O₂, LiNi_(0.92)Mn_(0.04)Co_(0.04)O₂, LiNi_(0.8)Co_(0.15)Al_(0.05)O₂, LiNiO₂, and combinations thereof.
 7. The cathode slurry of claim 1, wherein the solvent is water or a mixture of water and an alcohol.
 8. The cathode slurry of claim 7, wherein the alcohol is selected from the group consisting of ethanol, isopropanol, n-propanol, tert-butanol, n-butanol, and combinations thereof.
 9. The cathode slurry of claim 7, wherein the alcohol comprises from about 1% to about 30% of the total weight of the cathode slurry.
 10. The cathode slurry of claim 1, further comprising a conductive agent that is selected from the group consisting of carbon, carbon black, graphite, expanded graphite, graphene, graphene nanoplatelets, carbon fibers, carbon nano-fibers, graphitized carbon flake, carbon tubes, carbon nanotubes, activated carbon, mesoporous carbon and combinations thereof.
 11. The cathode slurry of claim 1, wherein the base has a boiling point of lower than 100° C. at a pressure of 1 atm.
 12. The cathode slurry of claim 1, wherein the base in the cathode slurry is at a concentration of from about 0.5% to about 3.5% by weight, based on the total weight of the cathode slurry.
 13. The cathode slurry of claim 1, wherein the cathode slurry has a pH of from about 11 to about 13.5.
 14. The cathode slurry of claim 1, wherein the binder material is selected from the group consisting of styrene-butadiene rubber, carboxymethyl cellulose, polyvinylidene fluoride, acrylonitrile copolymer, polyacrylic acid, polyacrylonitrile, poly(vinylidene fluoride)-hexafluoropropene, latex, a salt of alginic acid, and combinations thereof.
 15. The cathode slurry of claim 14, wherein the salt of alginic acid comprises a cation selected from the group consisting of Na, Li, K, Ca, NH₄, Mg, Al, and combinations thereof.
 16. The cathode slurry of claim 1, wherein lithium loss of the cathode active material is inhibited by a percentage from about 1 percent to about 50 percent.
 17. The cathode slurry of claim 1, wherein lithium loss of the cathode active material is inhibited by a percentage of about 10 percent or above.
 18. The cathode slurry of claim 1, wherein the cathode slurry has a solid content of from about 45% to about 75% by weight, based on the total weight of the cathode slurry.
 19. The cathode slurry of claim 1, wherein the cathode slurry is free of a dispersing agent selected from the group consisting of a cationic surfactant, an anionic surfactant, a nonionic surfactant, an amphoteric surfactant, and a polymeric acid. 